XENOY™ Resin T2RX2500UV PC PET
Plastic Granules
XENOY™ Resin T2RX2500UV PC PET Alloy Elastomer Modified
XENOY™ Resin T2RX2500UV is a medium-viscosity PC/PET blend with post-consumer recycled content. It is unfilled, UV stabilized, and elastomer modified. It offers 57 MPa tensile yield stress, 40 kJ/m² notched Izod impact at 23°C, and 136°C Vicat heat resistance.
Associated Documents
TDS - Americas
Typical property data
Physical Properties
- Density: 1.21 g/cm³ (ISO 1183)
- Melt Flow Rate, 265°C/2.16 kgf: 9 g/10 min (ASTM D1238)
- Melt Volume Rate, 265°C/1.2 kg: 4 cm³/10 min (ISO 1133)
- Mold Shrinkage, Flow: 0.5–0.8% (SABIC method)
- Mold Shrinkage, Cross-Flow: 0.5–0.8% (SABIC method)
- Water Absorption, 23°C/Saturated: 0.7% (ISO 62-1)
- Moisture Absorption, 23°C/50% RH: 0.2% (ISO 62)
Mechanical Properties
- Tensile Stress at Yield, 50 mm/min: 57 MPa (ISO 527)
- Tensile Strain at Yield, 50 mm/min: 5% (ISO 527)
- Tensile Strain at Break, 50 mm/min: 70% (ISO 527)
- Tensile Modulus, 1 mm/min: 2200 MPa (ISO 527)
- Flexural Stress at Yield, 2 mm/min: 80 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 2150 MPa (ISO 178)
Impact Properties
- Instrumented Dart Impact Total Energy, 23°C: 60 J (ASTM D3763)
- Notched Izod Impact, 80 × 10 × 4 mm, +23°C: 40 kJ/m² (ISO 180/1A)
- Notched Izod Impact, 80 × 10 × 4 mm, -30°C: 10 kJ/m² (ISO 180/1A)
- Charpy Impact, V-Notch Edgewise, 80 × 10 × 4 mm, span 62 mm, 23°C: 50 kJ/m² (ISO 179/1eA)
- Charpy Impact, V-Notch Edgewise, 80 × 10 × 4 mm, span 62 mm, -30°C: 10 kJ/m² (ISO 179/1eA)
Thermal Properties
- Vicat Softening Temperature, Rate B/120: 136°C (ISO 306)
- Heat Deflection Temperature, HDT/Af, 1.8 MPa, Flatwise, 80 × 10 × 4 mm, span 64 mm: 108°C (ISO 75/Af)
- Heat Deflection Temperature, HDT/Bf, 0.45 MPa, Flatwise, 80 × 10 × 4 mm, span 64 mm: 130°C (ISO 75/Bf)
Injection molding Processing
- Drying Temperature: 110–120°C
- Drying Time: 4–6 hours
- Maximum Moisture Content: 0.02%
- Melt Temperature: 265–275°C
- Nozzle Temperature: 260–275°C
- Front Zone 3 Temperature: 260–280°C
- Middle Zone 2 Temperature: 250–275°C
- Rear Zone 1 Temperature: 240–270°C
- Hopper Temperature: 60–80°C
- Mold Temperature: 60–100°C
Use & Applications
- Automotive exterior parts
- outdoor housings
- molded components requiring UV stability, impact strength, heat resistance, and PCR content