XENOY™ Resin T2RX5230 PC PET
Plastic Granules
XENOY™ Resin T2RX5230 PC PET Alloy Mineral Filled
XENOY™ Resin T2RX5230 is a 16% mineral filled PC/PET blend with post-consumer recycled content. It offers low CTE, high flow, high heat resistance, and 0.5–0.6% low shrinkage. Suitable for painted parts, body panels, housings, door handles, and EV components.
Associated Documents
TDS - Americas
Typical property data
Physical Properties
- Density: 1.34 g/cm³ (ISO 1183)
- Mold Shrinkage, Flow: 0.5–0.6% (SABIC Method)
- Mold Shrinkage, Cross Flow: 0.5–0.6% (SABIC Method)
- Water Absorption, 23°C Saturated: 0.42% (ISO 62-1)
- Moisture Absorption, 23°C / 50% RH: 0.14% (ISO 62)
- Melt Volume Rate, 265°C / 5.0 kg: 24 cm³/10 min (ISO 1133)
Mechanical Properties
- Tensile Stress, Yield, 5 mm/min: 56 MPa (ISO 527)
- Tensile Stress, Break, 5 mm/min: 21 MPa (ISO 527)
- Tensile Strain, Yield, 5 mm/min: 3.6% (ISO 527)
- Tensile Strain, Break, 5 mm/min: 14% (ISO 527)
- Tensile Modulus, 1 mm/min: 3430 MPa (ISO 527)
- Flexural Stress, Yield, 2 mm/min: 97 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 4120 MPa (ISO 178)
Impact Properties
- Izod Impact, Unnotched, 80 × 10 × 4 mm, +23°C: 140 kJ/m² (ISO 180/1U)
- Izod Impact, Unnotched, 80 × 10 × 4 mm, -30°C: 120 kJ/m² (ISO 180/1U)
- Izod Impact, Notched, 80 × 10 × 4 mm, +23°C: 7 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, -30°C: 5 kJ/m² (ISO 180/1A)
Thermal Properties
- CTE, -30°C to 80°C, Flow: 4.2E-05 1/°C (ISO 11359-2)
- CTE, -30°C to 80°C, Cross Flow: 9.6E-05 1/°C (ISO 11359-2)
- Vicat Softening Temperature, Rate B/50: 137°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 140°C (ISO 306)
- Heat Deflection Temperature, HDT/Af, 1.8 MPa, Flatwise, 80 × 10 × 4 mm, span 64 mm: 100°C (ISO 75/Af)
Injection Molding Processing
- Drying Temperature: 110–120°C
- Drying Time: 4–6 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 265–275°C
- Nozzle Temperature: 260–275°C
- Front Zone 3 Temperature: 260–280°C
- Middle Zone 2 Temperature: 250–275°C
- Rear Zone 1 Temperature: 240–270°C
- Hopper Temperature: 60–80°C
- Mold Temperature: 60–100°C
Use & Applications
- Body panels, spoilers
- Housings
- Door handles
- Spring-loaded part
- Fuel filler doors
- Medical device enclosures
- EV components