XENOY™ Resin PC PBT T2RX5630Q
Plastic Granules
XENOY™ Resin T2RX5630Q PC/PET Blend 19% Mineral Filled
XENOY™ Resin T2RX5630Q is a 19% mineral filled PC/PET blend with post-consumer recycled content. It offers low CTE, high heat resistance, low shrinkage, and strong dimensional stability for painted automotive, EV, and enclosure parts.
Associated Documents
TDS - Americas
Typical property data
Physical Properties
- Density: 1.35 g/cm³ (ISO 1183)
- Mold Shrinkage, Flow: 0.5–0.7% (SABIC method)
- Mold Shrinkage, Crossflow: 0.5–0.7% (SABIC method)
- Water Absorption, 23°C/Saturated: 0.42% (ISO 62-1)
- Moisture Absorption, 23°C / 50% RH: 0.14% (ISO 62)
- Melt Volume Rate, 265°C/5.0 kg: 16 cm³/10 min (ISO 1133)
Mechanical Properties
- Tensile Stress, Yield, 5 mm/min: 55 MPa (ISO 527)
- Tensile Stress, Break, 5 mm/min: 25 MPa (ISO 527)
- Tensile Strain, Yield, 5 mm/min: 3.3% (ISO 527)
- Tensile Strain, Break, 5 mm/min: 21% (ISO 527)
- Tensile Modulus, 1 mm/min: 4200 MPa (ISO 527)
- Flexural Stress, Yield, 2 mm/min: 91 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 4100 MPa (ISO 178)
Impact Properties
- Izod Impact, Unnotched, 80 × 10 × 4 mm, +23°C: 120 kJ/m² (ISO 180/1U)
- Izod Impact, Unnotched, 80 × 10 × 4 mm, -30°C: 80 kJ/m² (ISO 180/1U)
- Izod Impact, Notched, 80 × 10 × 4 mm, +23°C: 7 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, -30°C: 5 kJ/m² (ISO 180/1A)
Thermal Properties
- Coefficient of Thermal Expansion, Flow, -30°C to 80°C: 4.0E-05 1/°C (ISO 11359-2)
- Coefficient of Thermal Expansion, Crossflow, -30°C to 80°C: 11.4E-05 1/°C (ISO 11359-2)
- Vicat Softening Temperature, Rate B/50: 137°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 140°C (ISO 306)
- Heat Deflection Temperature, HDT/Af, 1.8 MPa, Flatwise, 80 × 10 × 4 mm, Span 64 mm: 108°C (ISO 75/Af)
Injection Molding Processing
- Drying Temperature: 110°C
- Drying Time: 4–6 hrs
- Drying Time, Cumulative: 8 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 260–275°C
- Nozzle Temperature: 255–270°C
- Front Zone 3 Temperature: 255–275°C
- Middle Zone 2 Temperature: 250–270°C
- Rear Zone 1 Temperature: 245–265°C
- Mold Temperature: 65–90°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 50–80 rpm
- Shot to Cylinder Size: 50–80%
- Vent Depth: 0.013–0.02 mm
Use & Applications
- Body panels
- Spoilers
- Housings
- Door handles
- Spring-loaded applications
- Fuel filler doors
- Medical device enclosures
- EV components