XENOY™ Resin X2300WX PC PET
Plastic Granules
XENOY™ Resin X2300WX Unreinforced PC+PET Alloy
XENOY™ Resin X2300WX is an unreinforced opaque PC+PET alloy. It offers chemical resistance, UV stability, and dimensional stability. It has 35 g/10 min MFR, 58 MPa tensile yield stress, and 640 J/m notched Izod impact at 23°C.
Associated Documents
TDS - Americas
Typical property data
Physical Properties
- Specific Gravity: 1.21 (ASTM D792)
- Mold Shrinkage, Flow, 3.2 mm: 0.8–1% (SABIC Method)
- Melt Flow Rate, 266°C/5.0 kgf: 35 g/10 min (ASTM D1238)
Mechanical Properties
- Tensile Stress at Yield, Type I, 50 mm/min: 58 MPa (ASTM D638)
- Tensile Stress at Break, Type I, 50 mm/min: 44 MPa (ASTM D638)
- Tensile Strain at Yield, Type I, 50 mm/min: 5% (ASTM D638)
- Tensile Strain at Break, Type I, 50 mm/min: 120% (ASTM D638)
- Tensile Modulus, 50 mm/min: 2410 MPa (ASTM D638)
- Flexural Stress at Yield, 1.3 mm/min, 50 mm Span: 86 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm Span: 2200 MPa (ASTM D790)
Impact Properties
- Notched Izod Impact, 23°C: 640 J/m (ASTM D256)
- Instrumented Dart Impact Total Energy, 23°C: 48 J (ASTM D3763)
Thermal Properties
- HDT, 0.45 MPa, 3.2 mm, Unannealed: 126°C (ASTM D648)
- HDT, 1.82 MPa, 3.2 mm, Unannealed: 110°C (ASTM D648)
- CTE, -40°C to 40°C, Flow: 7.2E-05 1/°C (ASTM E831)
- CTE, -40°C to 40°C, Cross Flow: 7.2E-05 1/°C (ASTM E831)
Injection Molding Processing
- Drying Temperature: 110°C
- Drying Time: 4–6 hrs
- Drying Time, Cumulative: 8 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 260–280°C
- Nozzle Temperature: 255–275°C
- Front Zone 3 Temperature: 260–280°C
- Middle Zone 2 Temperature: 255–275°C
- Rear Zone 1 Temperature: 250–270°C
- Mold Temperature: 65–95°C
- Back Pressure: 0.3–0.6 MPa
- Screw Speed: 50–80 rpm
- Shot to Cylinder Size: 50–80%
- Vent Depth: 0.013–0.02 mm
Use & Applications
- Outdoor housings
- Automotive exterior parts
- Trims
- UV-exposed molded components requiring chemical resistance and stable dimensions