XENOY™ Resin X2420 PC PBT
Plastic Granules
XENOY™ Resin X2420 PC PBT 10% Glass Filled Alloy
XENOY™ Resin X2420 is a 10% glass-filled PC/PBT resin for injection molding. It offers high flow, strong impact ductility, and stable stiffness. With 3800 MPa tensile modulus and 26 cm³/10 min MVR, it suits precise molded parts.
Associated Documents
TDS - Asia
Typical property data
Physical Properties
- Specific Gravity: 1.28 (ASTM D792)
- Density: 1.28 g/cm³ (ISO 1183)
- Mold Shrinkage, flow, 3.2 mm: 0.15–0.25% (SABIC method)
- Mold Shrinkage, xflow, 3.2 mm: 0.3–0.4% (SABIC method)
- Water Absorption, 23°C/saturated: 0.02% (ISO 62-1)
- Moisture Absorption, 23°C / 50% RH: 0.04% (ISO 62)
- Melt Volume Rate, MVR at 265°C / 2.16 kg: 12 cm³/10 min (ISO 1133)
- Melt Volume Rate, MVR at 300°C / 1.2 kg: 26 cm³/10 min (ISO 1133)
Mechanical Properties
- Tensile Stress, yield, Type I, 5 mm/min: 50 MPa (ASTM D638)
- Tensile Stress, break, Type I, 5 mm/min: 35 MPa (ASTM D638)
- Tensile Strain, yield, Type I, 5 mm/min: 3% (ASTM D638)
- Tensile Modulus, 5 mm/min: 3800 MPa (ASTM D638)
- Flexural Stress, yield, 1.3 mm/min, 50 mm span: 90 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm span: 3500 MPa (ASTM D790)
- Tensile Stress, yield, 5 mm/min: 51 MPa (ISO 527)
- Tensile Stress, break, 5 mm/min: 37 MPa (ISO 527)
- Tensile Strain, yield, 5 mm/min: 3% (ISO 527)
- Tensile Strain, break, 5 mm/min: 7% (ISO 527)
Impact Properties
- Izod Impact, unnotched, 23°C: 1600 J/m (ASTM D4812)
- Izod Impact, notched, 23°C: 205 J/m (ASTM D256)
- Instrumented Dart Impact Total Energy, 23°C: 36 J (ASTM D3763)
- Izod Impact, unnotched, 80 × 10 × 4 mm, +23°C: 110 kJ/m² (ISO 180/1U)
- Izod Impact, unnotched, 80 × 10 × 4 mm, -30°C: 74 kJ/m² (ISO 180/1U)
- Izod Impact, notched, 80 × 10 × 4 mm, +23°C: 14 kJ/m² (ISO 180/1A)
- Izod Impact, notched, 80 × 10 × 4 mm, -30°C: 8 kJ/m² (ISO 180/1A)
- Charpy Impact, V-notch edgewise, 80 × 10 × 4 mm, span 62 mm, 23°C: 15 kJ/m² (ISO 179/1eA)
- Charpy Impact, V-notch edgewise, 80 × 10 × 4 mm, span 62 mm, -30°C: 7 kJ/m² (ISO 179/1eA)
- Charpy Impact, unnotched edgewise, 80 × 10 × 4 mm, span 62 mm, 23°C: 95 kJ/m² (ISO 179/1eU)
- Charpy Impact, unnotched edgewise, 80 × 10 × 4 mm, span 62 mm, -30°C: 95 kJ/m² (ISO 179/1eU)
Thermal Properties
- Heat Deflection Temperature, 0.45 MPa, 3.2 mm, unannealed: 111°C (ASTM D648)
- Heat Deflection Temperature, 1.82 MPa, 3.2 mm, unannealed: 101°C (ASTM D648)
- Coefficient of Thermal Expansion, -40°C to 40°C, flow: 5.0E-05 1/°C (ASTM E831)
- Coefficient of Thermal Expansion, -40°C to 40°C, xflow: 8.0E-05 1/°C (ASTM E831)
- Coefficient of Thermal Expansion, 23°C to 80°C, flow: 4.0E-05 1/°C (ISO 11359-2)
- Coefficient of Thermal Expansion, 23°C to 80°C, xflow: 9.0E-05 1/°C (ISO 11359-2)
- Vicat Softening Temperature, Rate B/120: 118°C (ISO 306)
- Relative Temperature Index, Electrical: 75°C (UL 746B)
- Relative Temperature Index, Mechanical with impact: 75°C (UL 746B)
- Relative Temperature Index, Mechanical without impact: 75°C (UL 746B)
Electrical Properties
- Relative Temperature Index, Electrical: 75°C (UL 746B)
Flame Characteristics
- UL Recognized, 94HB Flame Class Rating: 0.4 mm (UL 94)
Injection molding Processing
- Drying Temperature: 95–105°C
- Drying Time: 3–4 hrs
- Drying Time, cumulative: 8 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 260–290°C
- Nozzle Temperature: 260–290°C
- Front Zone 3 Temperature: 255–290°C
- Middle Zone 2 Temperature: 255–290°C
- Rear Zone 1 Temperature: 250–280°C
- Hopper Temperature: 60–80°C
- Mold Temperature: 60–90°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 40–70 rpm
- Shot to Cylinder Size: 30–80%
- Vent Depth: 0.038–0.076 mm
Use & Applications
- Thin-wall or complex injection-molded parts
- Automotive components
- Housings
- Applications requiring high flow and impact strength