XENOY™ Resin X5100 PC PBT
Plastic Granules
XENOY™ Resin X5100 Impact-modified PC-PBT Blend Excellent Flow
XENOY™ Resin X5100 is an impact-modified PC-PBT resin with excellent flow. It offers 45 kJ/m² notched Izod impact at 23°C and 13 cm³/10 min MVR. It provides 2150 MPa tensile modulus, 1.22 g/cm³ density, and stable molding at 255–270°C.
Typical property data
Physical Properties
- Mold Shrinkage, flow: 0.7–1 % (SABIC method)
- Density: 1.22 g/cm³ (ISO 1183)
- Water Absorption, 23°C/saturated: 0.5 % (ISO 62-1)
- Moisture Absorption, 23°C / 50% RH: 0.15 % (ISO 62)
- Melt Volume Rate, MVR at 250°C / 2.16 kg: 13 cm³/10 min (ISO 1133)
- Melt Viscosity, 260°C, 1500 sec⁻¹: 215 Pa·s (ISO 11443)
Mechanical Properties
- Tensile Stress, yield, 50 mm/min: 54 MPa (ISO 527)
- Tensile Stress, break, 50 mm/min: 40 MPa (ISO 527)
- Tensile Strain, yield, 50 mm/min: 4.5 % (ISO 527)
- Tensile Strain, break, 50 mm/min: 100 % (ISO 527)
- Tensile Modulus, 1 mm/min: 2150 MPa (ISO 527)
- Flexural Stress, yield, 2 mm/min: 80 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 2050 MPa (ISO 178)
Impact Properties
- Izod Impact, notched, 80 × 10 × 4 mm, +23°C: 45 kJ/m² (ISO 180/1A)
- Izod Impact, notched, 80 × 10 × 4 mm, 0°C: 40 kJ/m² (ISO 180/1A)
- Izod Impact, notched, 80 × 10 × 4 mm, -10°C: 35 kJ/m² (ISO 180/1A)
- Izod Impact, notched, 80 × 10 × 4 mm, -20°C: 20 kJ/m² (ISO 180/1A)
- Izod Impact, notched, 80 × 10 × 4 mm, -30°C: 18 kJ/m² (ISO 180/1A)
- Charpy Impact, V-notch edgewise, 80 × 10 × 3 mm, span 62 mm, 0°C: 40 kJ/m² (ISO 179/1eA)
- Charpy Impact, V-notch edgewise, 80 × 10 × 4 mm, span 62 mm, 23°C: 50 kJ/m² (ISO 179/1eA)
- Charpy Impact, V-notch edgewise, 80 × 10 × 4 mm, span 62 mm, -30°C: 15 kJ/m² (ISO 179/1eA)
- Charpy Impact, unnotched edgewise, 80 × 10 × 4 mm, span 62 mm, -30°C: No break (ISO 179/1eU)
Thermal Properties
- Thermal Conductivity: 0.2 W/m·°C (ISO 8302)
- Coefficient of Thermal Expansion, -40°C to 40°C, x-flow: 8.0E-05 1/°C (ISO 11359-2)
- Coefficient of Thermal Expansion, 23°C to 80°C, flow: 8.5E-05 1/°C (ISO 11359-2)
- Ball Pressure Test, 75°C ± 2°C: Passes (IEC 60695-10-2)
- Vicat Softening Temperature, Rate A/50: 135°C (ISO 306)
- Vicat Softening Temperature, Rate B/50: 117°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 120°C (ISO 306)
- Heat Deflection Temperature, HDT/Be, 0.45 MPa edgewise, 120 × 10 × 4 mm, span 100 mm: 105°C (ISO 75/Be)
- Heat Deflection Temperature, HDT/Ae, 1.8 MPa edgewise, 120 × 10 × 4 mm, span 100 mm: 84°C (ISO 75/Ae)
Flame Characteristics
- Ball Pressure Test, 75°C ± 2°C: Passes (IEC 60695-10-2)
Processing Parameters
- Drying Temperature: 90–100°C
- Drying Time: 2–4 hrs
- Maximum Moisture Content: 0.02 %
- Melt Temperature: 255–270°C
- Nozzle Temperature: 250–265°C
- Front Zone 3 Temperature: 250–270°C
- Middle Zone 2 Temperature: 240–265°C
- Rear Zone 1 Temperature: 230–250°C
- Hopper Temperature: 40–60°C
- Mold Temperature: 60–80°C
Use & Applications
- Injection-molded automotive components
- housings
- trims
- parts requiring good flow and impact performance