XENOY™ Resin X5300WX PC PBT
Plastic Granules
XENOY™ Resin X5300WX Unreinforced Opaque PBT+PC Alloy
XENOY™ Resin X5300WX is an unreinforced opaque PC/PBT alloy. It offers UV stability, excellent weatherability, chemical resistance, and good mechanical strength. It delivers 747 J/m notched Izod impact at 23°C and 26 g/10 min melt flow for injection molding.
Typical property data
Physical Properties
- Specific Gravity: 1.23 (ASTM D792)
- Density: 1.23 g/cm³ (ISO 1183)
- Mold Shrinkage, Flow, 3.2 mm: 0.7–0.9% (SABIC Method)
- Melt Flow Rate, 266°C/5.0 kgf: 26 g/10 min (ASTM D1238)
- Melt Volume Rate, 265°C/5.0 kg: 25 cm³/10 min (ISO 1133)
- Water Absorption, 23°C/Saturated: 0.5% (ISO 62-1)
- Moisture Absorption, 23°C/50% RH: 0.15% (ISO 62)
Mechanical Properties
- Tensile Stress at Yield, Type I, 50 mm/min: 62 MPa (ASTM D638)
- Tensile Stress at Break, Type I, 50 mm/min: 51 MPa (ASTM D638)
- Tensile Strain at Yield, Type I, 50 mm/min: 5% (ASTM D638)
- Tensile Strain at Break, Type I, 50 mm/min: 110% (ASTM D638)
- Tensile Modulus, 50 mm/min: 2550 MPa (ASTM D638)
- Flexural Stress at Yield, 1.3 mm/min, 50 mm Span: 96 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm Span: 2480 MPa (ASTM D790)
- Tensile Stress at Yield, 50 mm/min: 62 MPa (ISO 527)
- Tensile Stress at Break, 50 mm/min: 51 MPa (ISO 527)
- Tensile Strain at Yield, 50 mm/min: 5% (ISO 527)
- Tensile Strain at Break, 50 mm/min: 110% (ISO 527)
- Tensile Modulus, 1 mm/min: 2250 MPa (ISO 527)
- Flexural Stress at Yield, 2 mm/min: 87 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 2180 MPa (ISO 178)
Impact Properties
- Notched Izod Impact, 23°C: 747 J/m (ASTM D256)
- Notched Izod Impact, -30°C: 180 J/m (ASTM D256)
- Instrumented Dart Impact Total Energy, 23°C: 71 J (ASTM D3763)
- Notched Izod Impact, 80 × 10 × 4 mm, +23°C: 50 kJ/m² (ISO 180/1A)
- Notched Izod Impact, 80 × 10 × 4 mm, -30°C: 15 kJ/m² (ISO 180/1A)
- Charpy Impact, 23°C, V-Notch Edgewise, 80 × 10 × 4 mm, Span 62 mm: 45 kJ/m² (ISO 179/1eA)
Thermal Properties
- Vicat Softening Temperature, Rate B/50: 135°C (ASTM D1525)
- Vicat Softening Temperature, Rate B/50: 120°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 124°C (ISO 306)
- HDT, 0.45 MPa, 3.2 mm, Unannealed: 101°C (ASTM D648)
- HDT, 1.82 MPa, 3.2 mm, Unannealed: 87°C (ASTM D648)
- HDT, 1.82 MPa, 6.4 mm, Unannealed: 88°C (ASTM D648)
- HDT/Af, 1.8 MPa, Flatwise, 80 × 10 × 4 mm, Span 64 mm: 89°C (ISO 75/Af)
- CTE, -40°C to 40°C, Flow: 7.02E-05 1/°C (ASTM E831)
- CTE, -40°C to 40°C, Cross Flow: 7.56E-05 1/°C (ASTM E831)
- CTE, -40°C to 40°C, Flow: 7.0E-05 1/°C (ISO 11359-2)
- CTE, -40°C to 40°C, Cross Flow: 7.5E-05 1/°C (ISO 11359-2)
Injection Molding Processing
- Drying Temperature: 110°C
- Drying Time: 4–6 hrs
- Drying Time, Cumulative: 8 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 260–275°C
- Nozzle Temperature: 255–270°C
- Front Zone 3 Temperature: 255–275°C
- Middle Zone 2 Temperature: 250–270°C
- Rear Zone 1 Temperature: 245–265°C
- Mold Temperature: 65–90°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 50–80 rpm
- Shot to Cylinder Size: 50–80%
- Vent Depth: 0.013–0.02 mm
Use & Applications
- Outdoor automotive components
- exterior trims
- housings
- weather-resistant molded parts