XENOY™ Resin X5600WX PC PBT
Plastic Granules
XENOY™ Resin X5600WX PC PBT
XENOY™ Resin X5600WX is an unreinforced PC/PBT alloy with UV stabilization and mold release. It offers chemical resistance, dimensional stability, and strong impact performance, including 800 J/m notched Izod impact at 23°C and 267 J/m at -30°C.
Associated Documents
TDS - Americas
Typical property data
Physical Properties
- Specific Gravity: 1.24 (ASTM D792)
- Density: 1.2 g/cm³ (ISO 1183)
- Mold Shrinkage, Flow, 3.2 mm: 0.7–0.9% (SABIC Method)
- Mold Shrinkage, Cross Flow, 3.2 mm: 0.7–0.9% (SABIC Method)
- Melt Flow Rate, 250°C/5.0 kgf: 4.1 g/10 min (ASTM D1238)
Mechanical Properties
- Tensile Stress at Yield, Type I, 50 mm/min: 61 MPa (ASTM D638)
- Tensile Stress at Break, Type I, 50 mm/min: 61 MPa (ASTM D638)
- Tensile Strain at Yield, Type I, 50 mm/min: 5.2% (ASTM D638)
- Tensile Strain at Break, Type I, 50 mm/min: 120% (ASTM D638)
- Tensile Modulus, 50 mm/min: 2480 MPa (ASTM D638)
- Flexural Stress at Yield, 1.3 mm/min, 50 mm span: 99 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm span: 2480 MPa (ASTM D790)
- Tensile Stress at Yield, 50 mm/min: 55 MPa (ISO 527)
- Tensile Stress at Break, 50 mm/min: 56 MPa (ISO 527)
- Tensile Strain at Yield, 50 mm/min: 4.5% (ISO 527)
- Tensile Strain at Break, 50 mm/min: 120% (ISO 527)
- Flexural Stress at Yield, 2 mm/min: 70 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 2150 MPa (ISO 178)
Impact Properties
- Notched Izod Impact, 23°C: 800 J/m (ASTM D256)
- Notched Izod Impact, -30°C: 267 J/m (ASTM D256)
- Instrumented Dart Impact Total Energy, 23°C: 54 J (ASTM D3763)
- Notched Izod Impact, 80 × 10 × 4 mm, +23°C: 50 kJ/m² (ISO 180/1A)
- Notched Izod Impact, 80 × 10 × 4 mm, -30°C: 20 kJ/m² (ISO 180/1A)
- Charpy Impact, 23°C, V-notch Edgewise, 80 × 10 × 4 mm, span 62 mm: 60 kJ/m² (ISO 179/1eA)
Thermal Properties
- Vicat Softening Temperature, Rate B/50: 130°C (ASTM D1525)
- Vicat Softening Temperature, Rate B/50: 130°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 132°C (ISO 306)
- Heat Deflection Temperature, 0.45 MPa, 3.2 mm, Unannealed: 120°C (ASTM D648)
- Heat Deflection Temperature, 1.82 MPa, 3.2 mm, Unannealed: 98°C (ASTM D648)
- HDT/Af, 1.8 MPa, Flatwise, 80 × 10 × 4 mm, span 64 mm: 95°C (ISO 75/Af)
- CTE, -40°C to 40°C, Flow: 6.9E-05 1/°C (ASTM E831)
- CTE, -40°C to 40°C, Cross Flow: 7.4E-05 1/°C (ASTM E831)
- CTE, -40°C to 40°C, Flow: 6.9E-05 1/°C (ISO 11359-2)
- CTE, -40°C to 40°C, Cross Flow: 7.4E-05 1/°C (ISO 11359-2)
Injection Molding Processing
- Drying Temperature: 110°C
- Drying Time: 4–6 hrs
- Cumulative Drying Time: 8 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 260–275°C
- Nozzle Temperature: 255–270°C
- Front Zone 3 Temperature: 255–275°C
- Middle Zone 2 Temperature: 250–270°C
- Rear Zone 1 Temperature: 245–265°C
- Mold Temperature: 65–90°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 50–80 rpm
- Shot to Cylinder Size: 50–80%
- Vent Depth: 0.013–0.02 mm
Use & Applications
- Outdoor molded parts
- automotive exterior components
- housings
- parts requiring UV stability and easy release