XENOY™ Resin X5630Q PC PET
Plastic Granules
XENOY™ Resin X5630Q PC/PET blend 19% Mineral-filled Low CTE
XENOY™ Resin X5630Q is a 19% mineral-filled PC/PET blend. It offers low CTE, high heat resistance, and stable dimensions. It has 0.5–0.7% mold shrinkage, 4200 MPa tensile modulus, and 110°C HDT. Suitable for painted automotive and EV parts.
Typical property data
Physical Properties
- Mold Shrinkage on Tensile Bar, flow: 0.5–0.7% (SABIC method)
- Melt Flow Rate, 265°C/5.0 kgf: 20 g/10 min (ASTM D1238)
- Density: 1.35 g/cm³ (ISO 1183)
- Water Absorption, 23°C/saturated: 0.42% (ISO 62-1)
- Moisture Absorption, 23°C/50% RH: 0.14% (ISO 62)
- Melt Volume Rate, 265°C/5.0 kg: 16 cm³/10 min (ISO 1133)
Mechanical Properties
- Tensile Stress, yield, 5 mm/min: 56 MPa (ISO 527)
- Tensile Stress, break, 5 mm/min: 41 MPa (ISO 527)
- Tensile Strain, yield, 5 mm/min: 3.3% (ISO 527)
- Tensile Strain, break, 5 mm/min: 14% (ISO 527)
- Tensile Modulus, 1 mm/min: 4200 MPa (ISO 527)
- Flexural Stress, yield, 2 mm/min: 92 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 4100 MPa (ISO 178)
Impact Properties
- Izod Impact, unnotched, 80 × 10 × 4 mm, +23°C: 121 kJ/m² (ISO 180/1U)
- Izod Impact, unnotched, 80 × 10 × 4 mm, -30°C: 80 kJ/m² (ISO 180/1U)
- Izod Impact, notched, 80 × 10 × 4 mm, +23°C: 7 kJ/m² (ISO 180/1A)
- Izod Impact, notched, 80 × 10 × 4 mm, -30°C: 5 kJ/m² (ISO 180/1A)
- Charpy Impact, V-notch Edgewise, 80 × 10 × 4 mm, span 62 mm, 23°C: 16 kJ/m² (ISO 179/1eA)
Thermal Properties
- CTE, -30°C to 80°C, flow: 3.8E-05 1/°C (ISO 11359-2)
- CTE, -30°C to 80°C, cross-flow: 1.0E-04 1/°C (ISO 11359-2)
- Vicat Softening Temperature, Rate B/50: 137°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 140°C (ISO 306)
- HDT/Af, 1.8 MPa, flatwise, 80 × 10 × 4 mm, span 64 mm: 110°C (ISO 75/Af)
Injection molding Processing
- Drying Temperature: 110°C
- Drying Time: 4–6 hours
- Drying Time, cumulative: 8 hours
- Maximum Moisture Content: 0.02%
- Melt Temperature: 260–275°C
- Nozzle Temperature: 255–270°C
- Front Zone 3 Temperature: 255–275°C
- Middle Zone 2 Temperature: 250–270°C
- Rear Zone 1 Temperature: 245–265°C
- Mold Temperature: 65–90°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 50–80 rpm
- Shot to Cylinder Size: 50–80%
- Vent Depth: 0.013–0.02 mm