XENOY™ Resin XL1339 PC PBT
Plastic Granules
XENOY™ Resin XL1339 High Heat PC/PBT Grade
XENOY™ Resin XL1339 is a high heat PC/PBT resin for applications where chemical resistance is not required. It offers 140°C Vicat softening temperature, 125°C HDT at 0.45 MPa, 55 MPa tensile yield stress, and strong impact performance down to -40°C.
Associated Documents
TDS - Europe
Typical property data
Physical Properties
- Density: 1.22 g/cm³ (ISO 1183)
- Mold Shrinkage, Flow: 0.5–0.8% (SABIC Method)
- Mold Shrinkage, Cross Flow: 0.5–0.8% (SABIC Method)
- Water Absorption, 23°C Saturated: 0.7% (ISO 62-1)
- Moisture Absorption, 23°C / 50% RH: 0.2% (ISO 62)
- Melt Volume Rate, 265°C / 1.2 kg: 4 cm³/10 min (ISO 1133)
Mechanical Properties
- Tensile Stress at Yield, 50 mm/min: 55 MPa (ISO 527)
- Tensile Stress at Break, 50 mm/min: 40 MPa (ISO 527)
- Tensile Strain at Yield, 50 mm/min: 5% (ISO 527)
- Tensile Strain at Break, 50 mm/min: 70% (ISO 527)
- Tensile Modulus, 1 mm/min: 2300 MPa (ISO 527)
- Flexural Stress at Yield, 2 mm/min: 80 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 2200 MPa (ISO 178)
- Ball Indentation Hardness, H358/30: 95 MPa (ISO 2039-1)
- Taber Abrasion, CS-17, 1 kg: 20 mg/1000 cycles (SABIC Method)
Impact Properties
- Izod Impact, Unnotched, 80 × 10 × 4 mm, +23°C: NB kJ/m² (ISO 180/1U)
- Izod Impact, Unnotched, 80 × 10 × 4 mm, -30°C: NB kJ/m² (ISO 180/1U)
- Izod Impact, Notched, 80 × 10 × 4 mm, +23°C: 40 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, -10°C: 38 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, -20°C: 35 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, -30°C: 25 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, -40°C: 15 kJ/m² (ISO 180/1A)
- Charpy Impact, V-Notch Edgewise, 80 × 10 × 4 mm, Span 62 mm, 23°C: 45 kJ/m² (ISO 179/1eA)
- Charpy Impact, Notched, 23°C: 50 kJ/m² (ISO 179/2C)
- Charpy Impact, V-Notch Edgewise, 80 × 10 × 4 mm, Span 62 mm, -30°C: 35 kJ/m² (ISO 179/1eA)
- Charpy Impact, Notched, -20°C: 10 kJ/m² (ISO 179/2C)
- Charpy Impact, Notched, -30°C: 7 kJ/m² (ISO 179/2C)
- Charpy Impact, Unnotched Edgewise, 80 × 10 × 4 mm, Span 62 mm, 23°C: NB kJ/m² (ISO 179/1eU)
- Charpy Impact, Unnotched Edgewise, 80 × 10 × 4 mm, Span 62 mm, -30°C: NB kJ/m² (ISO 179/1eU)
Thermal Properties
- Vicat Softening Temperature, Rate A/50: 140°C (ISO 306)
- Vicat Softening Temperature, Rate B/50: 130°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 135°C (ISO 306)
- Heat Deflection Temperature, 0.45 MPa, Edgewise, 120 × 10 × 4 mm, Span 100 mm: 125°C (ISO 75/Be)
- Heat Deflection Temperature, 1.8 MPa, Edgewise, 120 × 10 × 4 mm, Span 100 mm: 105°C (ISO 75/Ae)
- Thermal Conductivity: 0.18 W/m·°C (ISO 8302)
- Coefficient of Thermal Expansion, 23°C to 80°C, Flow: 7.5E-05 1/°C (ISO 11359-2)
- Coefficient of Thermal Expansion, 23°C to 80°C, Cross Flow: 8.0E-05 1/°C (ISO 11359-2)
- Ball Pressure Test, 125°C ± 2°C: Passes (IEC 60695-10-2)
Electrical Properties
- Volume Resistivity: >1.0E+14 Ω·cm (IEC 60093)
- Surface Resistivity, ROA: >1.0E+15 Ω (IEC 60093)
- Dielectric Strength, in Oil, 3.2 mm: 17 kV/mm (IEC 60243-1)
- Relative Permittivity, 50/60 Hz: 3.3 (IEC 60250)
- Relative Permittivity, 1 MHz: 3.1 (IEC 60250)
- Dissipation Factor, 50/60 Hz: 0.002 (IEC 60250)
- Dissipation Factor, 1 MHz: 0.02 (IEC 60250)
- Comparative Tracking Index: 600 V (IEC 60112)
Flame Characteristics
- UL 94 Flame Class Rating, 94HB: 1.5 mm (UL 94 by SABIC-IP)
- Glow Wire Flammability Index, 750°C: Passes at 2.7 mm (IEC 60695-2-12)
Injection Molding Processing
- Drying Temperature: 110–120°C
- Drying Time: 4–6 hours
- Maximum Moisture Content: 0.02%
- Melt Temperature: 265–275°C
- Nozzle Temperature: 260–275°C
- Front Zone 3 Temperature: 260–280°C
- Middle Zone 2 Temperature: 250–275°C
- Rear Zone 1 Temperature: 240–270°C
- Hopper Temperature: 60–80°C
- Mold Temperature: 60–100°C
Use & Applications
- High-heat molded parts and components that require thermal performance but do not require strong chemical resistance.