Suke Plastics 3016 PC ABS
Suke 3016 PC/ABS Resin Flame Retardant Grade
Suke 3016 is a premium PC/ABS blend offering superior impact strength and halogen-free safety. Perfect for electrical enclosures, durable office equipment, and router housings, it combines toughness with excellent processability for reliable, high-quality industrial components.
Plastic Granules
Download PDF
Typical property data
Physical Properties
- Density: 1.18 g/cm³ (ASTM D792, at 23°C).
- Mold Shrinkage: 0.4–0.8% (Internal standard, 2 mm).
Mechanical Properties
- Tensile Strength: 55 MPa (ASTM D638, 50 mm/min).
- Elongation at Break: 50% (ASTM D638, 50 mm/min).
- Flexural Strength: 88 MPa (ASTM D790, 2 mm/min).
- Flexural Modulus: 2100 MPa (ASTM D790, 2 mm/min).
Impact Properties
- Izod Notched Impact Strength: 60 KJ/m² (ASTM D256, 3.2 mm, at 23°C).
Thermal Properties
- Heat Distortion Temperature (HDT): 88°C (ASTM D648, 1.8 MPa, 6.4 mm).
Flame Characteristics
- Flammability: UL94 Class V0 (1.5 mm).
Injection Molding
- Pre-drying Temperature and Time: 80–90°C, 3 hours.
- Injection Pressure: 60–100 MPa.
- Injection Speed: 50–80.
- Mold Temperature: 80°C.
- Maximum Processing Temperature: 280°C.
- Melt Temperature: 260°C.
- Cylinder Temperature:
- Feeding Section: 230–250°C.
- Compression Section: 240–260°C.
- Nozzle: 250–270°C.
Use & Applications
- Electrical & Electronic Components: Connectors, sockets, switch housings.
- Office Supplies: Printer panels, scanner covers, durable keyboard frames.
- Router & Networking Gear: Impact-resistant casings and structural parts.
Features & Benefits
Safety & Compliance Guaranteed
Halogen-free and UL94 V0 rated (at 1.5mm), Suke 3016 meets strict fire safety and environmental regulations. Ideal for electronics and consumer goods requiring reliable flame resistance without hazardous additives.
Exceptional Impact Resistance
With 60 KJ/m² Izod notched impact strength, it withstands drops, impacts, and stress – perfect for protective casings, tool housings, and components prone to rough handling.
Optimized Processing Efficiency
It features high melt flow (21 g/10min) and fast drying (3hrs at 85°C), reducing cycle times and energy use. Ensures smooth molding of complex parts with minimal warpage.