Suke Plastics 5983R PC Resin
Plastic Granules
Suke 5983R PC Resin Flame Retardant Grade
Suke 5983R is an industrial-grade halogen-free PC resin engineered for high toughness and flame resistance. Ideal for demanding electronics applications, it combines durability, safety compliance, and ease of processing—perfect for components like charger heads.
Download PDF
ASTM TDS
Typical property data
Physical Properties
- Density: 1.2 g/cm³ (ASTM D792, 23°C)
Mechanical Properties
- Tensile Strength: 64 MPa (ASTM D638, 50 mm/min)
- Elongation at Break: 100% (ASTM D638, 50 mm/min)
- Flexural Strength: 88 MPa (ASTM D790, 2 mm/min)
- Flexural Modulus: 2250 MPa (ASTM D790, 2 mm/min)
Impact Properties
- Impact Strength (Notched Izod): 70 KJ/m² (ASTM D256, 3.2 mm, 23°C)
Thermal Properties
- Heat Distortion Temperature (HDT): 123°C (ASTM D648, 1.8 MPa, 6.4 mm)
Flame Characteristics
- Flammability: V-0 (UL94, 1.5 mm thickness)
Injection Molding
- Pre-drying Condition: 110-120°C, 4 hours
- Injection Pressure: 60-100 MPa
- Mold Temperature: 100°C
- Processing Temperatures:
- Melt Temperature: 280-320°C
- Cylinder Temperatures:
- Feeding: 240-260°C
- Compressing: 270-290°C
- Nozzle: 280-300°C
Use & Applications
- Charger Heads
Features & Benefits
Halogen-Free Safety Compliance
This eco-friendly material eliminates toxic fumes, meeting strict global regulations (UL94 V0 at 1.5mm). Perfect for consumer electronics where fire safety is non-negotiable.
Superior Impact Resistance
With 70 KJ/m² IZOD notched impact strength, 5983R withstands drops and shocks. Reduces product failure rates in rugged environments, saving replacement costs.
Optimized Processing Stability
Pre-dried at 110–120°C and processed up to 320°C, it flows smoothly (MFR: 10g/10min) and resists warping (0.5–0.7% shrinkage). Lowers defect risks in high-volume production.