TORAY Toyolac™ 900 352A U
Plastic Granules
Toyolac™ 900 352A U Transparent Grade Middle Impact Strength
Toyolac™ 900 352A U is a transparent grade MABS resin offering middle impact strength, tailored for applications demanding clarity, durability, and moldability. Its reliable performance and adaptability make it an exceptional choice for industries like electronics, appliances, and toy manufacturing.
Typical property data
Physical Properties
- Density: 1090 kg/m³ (ISO 1183, 23 °C)
- Melt Flow Rate (MFR): 20 g/10 min (ISO 1133, 220 °C / 10 kg)
- Mold Shrinkage: 0.4%−0.6% (ASTM D955, 23 °C / 50% RH)
Mechanical Properties
- Tensile Strength at Yield: 53MPa (ISO 527, at 50 mm/min)
- Tensile Elongation at Break: 12% (ISO 527, at 50 mm/min)
- Tensile Modulus: 2400MPa (ISO 527, at 1 mm/min)
- Flexural Strength: 76MPa (ISO 178, at 2 mm/min)
- Flexural Modulus: 2310MPa (ISO 178, at 2 mm/min)
Impact Properties
- Charpy Notched Impact Strength: 12 kJ/m² (ISO 179/1eA, 23 °C / 50% RH)
Thermal Properties
- Deflection Temperature Under Load (DTUL): 76 °C (ISO 75, at 1.8 MPa / 120 °C/hr)
Optical Properties
- Light Transmittance: (ASTM D1003, at 3 mm thickness)
- Haze: (ASTM D1003, at 3 mm thickness)
Flame Characteristics
- Flammability Classification: HB (UL 94, File No. E41797)
Use & Applications
- E&E Products
- Household and Office Appliances
- Toys
Features & Benefits
1. Exceptional Optical Clarity
With 87% light transmittance and low haze (2%), this MABS resin ensures crystal-clear transparency ideal for visually appealing components.
2. High-Impact Durability
Its Charpy Impact Strength (12 kJ/m²) offers reliable toughness, making it suitable for demanding applications like electronics and appliances.
3. Consistent Processability
The Melt Flow Rate (20 g/10 min) and controlled shrinkage (0.4–0.6%) ensure precise, repeatable molding results for superior quality.