ULTEM™ Resin 2110
Plastic Granules
ULTEM™ Resin 2110 Enhanced Flow 10% Glass Fiber Filled
ULTEM™ Resin 2110 is a 10% glass fiber reinforced, enhanced-flow PEI resin with Tg 217°C, HDT 207°C, UL 94 V-0 at ≥0.38 mm, F1 rating, and 170°C RTI performance for demanding electrical, automotive, aerospace, and industrial applications.
Typical property data
Physical Properties
- Specific Gravity: 1.34 (ASTM D792)
- Melt Flow Rate: 11.3 g/10 min at 337°C / 6.6 kgf (ASTM D1238)
Mechanical Properties
- Tensile Stress at Yield: 114 MPa at 5 mm/min, Type I (ASTM D638)
- Tensile Stress at Break: 115 MPa at 5 mm/min, Type I (ASTM D638)
- Tensile Strain at Break: 6% at 5 mm/min, Type I (ASTM D638)
- Tensile Modulus: 4610 MPa at 5 mm/min (ASTM D638)
- Flexural Stress at Break: 199 MPa at 2.6 mm/min, 100 mm span (ASTM D790)
- Flexural Modulus: 5240 MPa at 2.6 mm/min, 100 mm span (ASTM D790)
- Notched Izod Impact Strength: 48 J/m at 23°C (ASTM D256)
- Reverse Notched Izod Impact Strength: 400 J/m at 3.2 mm (ASTM D256)
Thermal Properties
- Glass Transition Temperature: 217°C — stated in product description
- Heat Deflection Temperature: 207°C at 1.82 MPa, 6.4 mm, unannealed (ASTM D648)
- Relative Temperature Index, Electrical: 170°C (UL 746B)
- Relative Temperature Index, Mechanical with Impact: 170°C (UL 746B)
- Relative Temperature Index, Mechanical without Impact: 170°C (UL 746B)
Electrical Properties
- Comparative Tracking Index: PLC 4 (UL 746A)
- Hot-Wire Ignition, HWI PLC 1: ≥3 mm (UL 746A)
- Hot-Wire Ignition, HWI PLC 2: ≥1.5 mm (UL 746A)
- High Amp Arc Ignition, HAI PLC 3: ≥1.5 mm (UL 746A)
- High Amp Arc Ignition, HAI PLC 4: ≥3 mm (UL 746A)
- High Voltage Arc Tracking Rate: PLC 2 (UL 746A)
- Arc Resistance, Tungsten: PLC 6 (ASTM D495)
Flame Characteristics
- UL Flame Rating: UL 94 V-0 at ≥0.38 mm (UL 94)
- UL 5VA Listing: Listed in product description
- UL Yellow Card Reference: E45587-236982
- UV-Light, Water Exposure / Immersion Rating: F1 (UL 746C)
Processing Parameters
- Processing Method: Injection molding
- Drying Temperature: 150°C
- Drying Time: 4–6 hrs
- Cumulative Drying Time: 24 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 350–400°C
- Nozzle Temperature: 345–400°C
- Front Zone 3 Temperature: 345–400°C
- Middle Zone 2 Temperature: 340–400°C
- Rear Zone 1 Temperature: 330–400°C
- Mold Temperature: 135–165°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 40–70 rpm
- Shot-to-Cylinder Size: 40–60%
- Vent Depth: 0.025–0.076 mm