ULTEM™ Resin 2110EPR
Plastic Granules
ULTEM™ Resin 2110EPR High Flow 20% Glass Fiber Filled
ULTEM™ Resin 2110EPR is a 20% glass-filled high-flow PEI resin. It delivers high stiffness, 213°C HDT, UL94 V-0 flame rating, and enhanced electroplatability. A strong choice for precision molded parts in electrical, automotive, and industrial applications.
Typical property data
Physical Properties
- Specific Gravity: 1.39 (ASTM D792)
- Mold Shrinkage, Flow, 3.2 mm: 0.5–0.7% (SABIC method)
- Mold Shrinkage, Cross-flow, 3.2 mm: 0.5–0.7% (SABIC method)
- Melt Flow Rate, 337°C/6.6 kgf: 13 g/10 min (ASTM D1238)
Mechanical Properties
- Tensile Stress at Yield, Type I, 5 mm/min: 137 MPa (ASTM D638)
- Tensile Stress at Break, Type I, 5 mm/min: 137 MPa (ASTM D638)
- Tensile Strain at Yield, Type I, 5 mm/min: 3% (ASTM D638)
- Tensile Strain at Break, Type I, 5 mm/min: 3% (ASTM D638)
- Tensile Modulus, 5 mm/min: 6890 MPa (ASTM D638)
- Flexural Stress at Yield, 1.3 mm/min, 50 mm span: 206 MPa (ASTM D790)
- Flexural Stress at Break, 2.6 mm/min, 100 mm span: 206 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm span: 6890 MPa (ASTM D790)
- Flexural Modulus, 2.6 mm/min, 100 mm span: 6890 MPa (ASTM D790)
Impact Properties
- Izod Impact, Unnotched, 23°C: 587 J/m (ASTM D4812)
- Izod Impact, Notched, 23°C: 80 J/m (ASTM D256)
- Instrumented Dart Impact Total Energy, 23°C: 14 J (ASTM D3763)
Thermal Properties
- Glass Transition Temperature, Tg: 217°C
- Vicat Softening Temperature, Rate B/50: 210°C (ASTM D1525)
- Heat Deflection Temperature, 0.45 MPa, 3.2 mm, Unannealed: 211°C (ASTM D648)
- Heat Deflection Temperature, 1.82 MPa, 3.2 mm, Unannealed: 206°C (ASTM D648)
- Heat Deflection Temperature, 0.45 MPa, 6.4 mm, Unannealed: 213°C (ASTM D648)
- Heat Deflection Temperature, 1.82 MPa, 6.4 mm, Unannealed: 208°C (ASTM D648)
- Coefficient of Thermal Expansion, -40°C to 40°C, Flow: 3.6E-05 1/°C (ASTM E831)
- Coefficient of Thermal Expansion, -40°C to 40°C, Cross-flow: 7.2E-05 1/°C (ASTM E831)
- Relative Temperature Index, Electrical: 105°C (UL 746B)
- Relative Temperature Index, Mechanical with Impact: 105°C (UL 746B)
- Relative Temperature Index, Mechanical without Impact: 105°C (UL 746B)
Electrical Properties
- Comparative Tracking Index, CTI: PLC 4 (UL 746A)
- Hot-Wire Ignition, HWI, PLC 1: ≥3 mm (UL 746A)
- Hot-Wire Ignition, HWI, PLC 2: ≥1.5 mm (UL 746A)
- Hot-Wire Ignition, HWI, PLC 3: ≥0.75 mm (UL 746A)
- Hot-Wire Ignition, HWI, PLC 4: ≥0.4 mm (UL 746A)
- High Amp Arc Ignition, HAI, PLC 4: ≥0.4 mm (UL 746A)
- High Voltage Arc Track Rate: PLC 4 (UL 746A)
- Arc Resistance, Tungsten: PLC 6 (ASTM D495)
Flame Characteristics
- UL Recognized, 94V-0 Flame Class Rating: ≥0.4 mm (UL 94)
- Flame Listing in Description: UL94 V-0 and 5VA
Processing Performance
- Melt Flow Rate, 337°C/6.6 kgf: 13 g/10 min (ASTM D1238)
- Mold Shrinkage, Flow, 3.2 mm: 0.5–0.7% (SABIC method)
- Mold Shrinkage, Cross-flow, 3.2 mm: 0.5–0.7% (SABIC method)
- Internal Mold Release: Yes
- High Flow Grade: Yes
- Enhanced Electroplatability: Yes
Certifications & Compliance
- ECO Conforming: Yes
- UL94 V-0 Listing: Yes
- UL94 5VA Listing: Yes
- UL Yellow Card Reference: E207780-104152645
- UL Recognized 94V-0 Flame Class Rating: ≥0.4 mm (UL 94)
Use & Applications
- Automotive under-the-hood components
- Heavy truck parts
- Aerospace components
- Motorcycle and specialty vehicle parts
- Building components
- Water management parts
- Electrical and electronic housings
- Energy management components
- Circuit board and additive applications
- Lighting components
- Printer and copier parts
- Speaker and earphone components
- Wireless communication parts
- Healthcare and surgical device components
- Pharmaceutical packaging and drug delivery parts
- Industrial electrical components
- Material handling parts
- Eyewear components
- Rail transportation components
- Industrial packaging