ULTEM™ Resin 2200R
Plastic Granules
ULTEM™ Resin 2200R Standard Flow 20% Glass Fiber Filled
ULTEM™ Resin 2200R is a 20% glass fiber reinforced PEI with internal mold release. It delivers high stiffness, 210°C HDT, low shrinkage, strong insulation, and UL94 V-0 flame resistance for precision molded parts.
Typical property data
Physical Properties
- Specific Gravity: 1.42 (ASTM D792)
- Water Absorption, 23°C / 24 hrs: 0.19% (ASTM D570)
- Water Absorption, 23°C / Saturated: 1.1% (ASTM D570)
- Mold Shrinkage, flow, 3.2 mm: 0.3–0.5% (SABIC Method)
- Melt Flow Rate, 337°C / 6.6 kgf: 6.5 g/10 min (ASTM D1238)
Mechanical Properties
- Tensile Stress at Break, Type I, 5 mm/min: 131 MPa (ASTM D638)
- Tensile Strain at Break, Type I, 5 mm/min: 4% (ASTM D638)
- Tensile Modulus, 5 mm/min: 6890 MPa (ASTM D638)
- Flexural Stress at Break, 2.6 mm/min, 100 mm span: 227 MPa (ASTM D790)
- Flexural Modulus, 2.6 mm/min, 100 mm span: 6890 MPa (ASTM D790)
- Hardness, Rockwell M: 114 (ASTM D785)
Impact Properties
- Izod Impact, Unnotched, 23°C: 480 J/m (ASTM D4812)
- Izod Impact, Notched, 23°C: 90 J/m (ASTM D256)
- Izod Impact, Reverse Notched, 3.2 mm: 512 J/m (ASTM D256)
Thermal Properties
- Glass Transition Temperature: 217°C Tg
- Vicat Softening Temperature, Rate B/50: 220°C (ASTM D1525)
- HDT, 0.45 MPa, 6.4 mm, unannealed: 210°C (ASTM D648)
- HDT, 1.82 MPa, 6.4 mm, unannealed: 210°C (ASTM D648)
- Coefficient of Thermal Expansion, -20°C to 150°C, flow: 2.1E-05 1/°C (ASTM D150)
- Relative Temperature Index, Electrical: 170°C (UL 746B)
- Relative Temperature Index, Mechanical with Impact: 170°C (UL 746B)
- Relative Temperature Index, Mechanical without Impact: 170°C (UL 746B)
Electrical Properties
- Volume Resistivity: 7.E+16 Ω·cm (ASTM D257)
- Dielectric Strength, in oil, 1.6 mm: 26.3 kV/mm (ASTM D149)
- Relative Permittivity, 1 kHz: 3.5 (ASTM D150)
- Dissipation Factor, 1 kHz: 0.0015 (ASTM D150)
- Dissipation Factor, 2450 MHz: 0.0049 (ASTM D150)
- Comparative Tracking Index, UL PLC: PLC 4 (UL 746A)
- Hot-Wire Ignition, HWI PLC 1: ≥3 mm (UL 746A)
- Hot-Wire Ignition, HWI PLC 2: ≥1.5 mm (UL 746A)
- High Amp Arc Ignition, HAI PLC 3: ≥1.5 mm (UL 746A)
- High Amp Arc Ignition, HAI PLC 4: ≥3 mm (UL 746A)
- High Voltage Arc Track Rate, PLC: PLC 2 (UL 746A)
- Arc Resistance, Tungsten PLC: PLC 6 (ASTM D495)
Flame Characteristics
- UL Recognized 94V-0 Flame Class Rating: ≥0.38 mm (UL 94)
- UV-Light / Water Exposure / Immersion Rating: F1 (UL 746C)
- Oxygen Index, LOI: 50% (ASTM D2863)
- NBS Smoke Density, Flaming, Ds 4 min: 1.3 (ASTM E662)
- UL94 Positioning: ULTEM™ Resin 2200R is listed for UL94 V-0 and 5VA flame performance.
Processing Parameters
- Drying Temperature: 150°C
- Drying Time: 4–6 hrs
- Drying Time, Cumulative: 24 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 350–400°C
- Nozzle Temperature: 345–400°C
- Front Zone 3 Temperature: 345–400°C
- Middle Zone 2 Temperature: 340–400°C
- Rear Zone 1 Temperature: 330–400°C
- Mold Temperature: 135–165°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 40–70 rpm
- Shot to Cylinder Size: 40–60%
- Vent Depth: 0.025–0.076 mm
Use & Applications
- Automotive
- Aerospace
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare
- Mass Transportation Rail components
- Industrial packaging