ULTEM™ Resin 2210
Plastic Granules
ULTEM™ Resin 2210 Enhanced Flow 20% Glass Fiber Reinforced
ULTEM™ Resin 2210 is a 20% glass fiber reinforced PEI with enhanced flow. It offers high stiffness, 211°C HDT, UL94 V-0 flame rating, and strong dimensional stability. Choose it for demanding heat, electrical, and precision molded parts.
Typical property data
Physical Properties
- Specific Gravity: 1.42 (ASTM D792)
- Melt Flow Rate: 8.4 g/10 min at 337°C / 6.6 kgf (ASTM D1238)
Mechanical Properties
- Tensile Stress at Break: 139 MPa at 5 mm/min, Type I (ASTM D638)
- Tensile Strain at Break: 4% at 5 mm/min, Type I (ASTM D638)
- Tensile Modulus: 6890 MPa at 5 mm/min (ASTM D638)
- Flexural Stress at Break: 227 MPa at 2.6 mm/min, 100 mm span (ASTM D790)
- Flexural Modulus: 6890 MPa at 2.6 mm/min, 100 mm span (ASTM D790)
- Rockwell Hardness: M114 (ASTM D785)
- Izod Impact, Unnotched: 475 J/m at 23°C (ASTM D4812)
- Izod Impact, Notched: 64 J/m at 23°C (ASTM D256)
- Izod Impact, Reverse Notched: 453 J/m at 3.2 mm (ASTM D256)
Thermal Properties
- Glass Transition Temperature, Tg: 217°C
- Coefficient of Thermal Expansion, Flow: 2.1E-05 1/°C from -40°C to 150°C (ISO 11359-2)
- Coefficient of Thermal Expansion, Cross Flow: 4.9E-05 1/°C from -40°C to 150°C (ISO 11359-2)
- Vicat Softening Temperature: 225°C, Rate B/50 (ASTM D1525)
- Heat Deflection Temperature: 210°C at 0.45 MPa, 6.4 mm, unannealed (ASTM D648)
- Heat Deflection Temperature: 211°C at 1.82 MPa, 6.4 mm, unannealed (ASTM D648)
- Relative Temperature Index, Electrical: 170°C (UL 746B)
- Relative Temperature Index, Mechanical with Impact: 170°C (UL 746B)
- Relative Temperature Index, Mechanical without Impact: 170°C (UL 746B)
Electrical Properties
- Comparative Tracking Index, CTI: PLC 4 (UL 746A)
- Hot-Wire Ignition, HWI: PLC 1 at ≥3 mm (UL 746A)
- Hot-Wire Ignition, HWI: PLC 2 at ≥1.5 mm (UL 746A)
- High Amp Arc Ignition, HAI: PLC 3 at ≥1.5 mm (UL 746A)
- High Amp Arc Ignition, HAI: PLC 4 at ≥3 mm (UL 746A)
- High Voltage Arc Tracking Rate: PLC 2 (UL 746A)
- Arc Resistance, Tungsten: PLC 6 (ASTM D495)
Flame Characteristics
- UL 94 Flame Rating: V-0 at ≥0.38 mm (UL 94)
- UV-Light / Water Exposure / Immersion Rating: F1 (UL 746C)
- Oxygen Index, LOI: 50% (ASTM D2863)
- NBS Smoke Density, Flaming, Ds at 4 min: 1.3 (ASTM E662)
- 5VA Listing
Processing Parameters
- Recommended Process: Injection molding
- Drying Temperature: 150°C
- Drying Time: 4–6 hrs
- Maximum Cumulative Drying Time: 24 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 350–400°C
- Nozzle Temperature: 345–400°C
- Front Zone 3 Temperature: 345–400°C
- Middle Zone 2 Temperature: 340–400°C
- Rear Zone 1 Temperature: 330–400°C
- Mold Temperature: 135–165°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 40–70 rpm
- Shot to Cylinder Size: 40–60%
- Vent Depth: 0.025–0.076 mm
Use & Applications
Automotive under-hood components
Heavy truck electrical and thermal parts
Aerospace structural and electrical components
Circuit board and additive components
Electrical insulation parts
Energy management devices
Lighting components
Printer and copier components
Wireless communication components
Surgical device components
Pharmaceutical packaging and drug delivery parts
Industrial electrical components
Rail and mass transportation components
Water management components
High-temperature appliance parts