ULTEM™ Resin 2210EPR
Plastic Granules
ULTEM™ Resin 2210EPR High-flow 20% Glass Fiber Filled
ULTEM™ Resin 2210EPR is a 20% glass fiber reinforced PEI resin. It offers high flow, strong stiffness, heat resistance, and enhanced electroplatability. UL94 V-0 and 5VA ratings support demanding electrical and industrial parts.
Typical property data
Physical Properties
- Specific Gravity: 1.39 (ASTM D792)
- Mold Shrinkage, Flow, 3.2 mm: 0.5–0.7% (SABIC Method)
- Mold Shrinkage, Cross Flow, 3.2 mm: 0.5–0.7% (SABIC Method)
- Melt Flow Rate, 337°C/6.6 kgf: 13 g/10 min (ASTM D1238)
Mechanical Properties
- Tensile Stress, Yield, Type I, 5 mm/min: 137 MPa (ASTM D638)
- Tensile Stress, Break, Type I, 5 mm/min: 137 MPa (ASTM D638)
- Tensile Strain, Yield, Type I, 5 mm/min: 3% (ASTM D638)
- Tensile Strain, Break, Type I, 5 mm/min: 3% (ASTM D638)
- Tensile Modulus, 5 mm/min: 6890 MPa (ASTM D638)
- Flexural Stress, Yield, 1.3 mm/min, 50 mm Span: 206 MPa (ASTM D790)
- Flexural Stress, Break, 2.6 mm/min, 100 mm Span: 206 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm Span: 6890 MPa (ASTM D790)
- Flexural Modulus, 2.6 mm/min, 100 mm Span: 6890 MPa (ASTM D790)
- Izod Impact, Unnotched, 23°C: 587 J/m (ASTM D4812)
- Izod Impact, Notched, 23°C: 80 J/m (ASTM D256)
- Instrumented Dart Impact Total Energy, 23°C: 14 J (ASTM D3763)
Thermal Properties
- Glass Transition Temperature, Tg: 217°C (datasheet description)
- Vicat Softening Temperature, Rate B/50: 210°C (ASTM D1525)
- HDT, 0.45 MPa, 3.2 mm, Unannealed: 211°C (ASTM D648)
- HDT, 1.82 MPa, 3.2 mm, Unannealed: 206°C (ASTM D648)
- HDT, 0.45 MPa, 6.4 mm, Unannealed: 213°C (ASTM D648)
- HDT, 1.82 MPa, 6.4 mm, Unannealed: 208°C (ASTM D648)
- CTE, -40°C to 40°C, Flow: 3.6E-05 1/°C (ASTM E831)
- CTE, -40°C to 40°C, Cross Flow: 7.2E-05 1/°C (ASTM E831)
- Relative Temperature Index, Electrical: 105°C (UL 746B)
- Relative Temperature Index, Mechanical with Impact: 105°C (UL 746B)
- Relative Temperature Index, Mechanical without Impact: 105°C (UL 746B)
Electrical Properties
- Comparative Tracking Index, UL, PLC: 4 PLC Code (UL 746A)
- Hot-Wire Ignition, HWI, PLC 1: ≥3 mm (UL 746A)
- Hot-Wire Ignition, HWI, PLC 2: ≥1.5 mm (UL 746A)
- Hot-Wire Ignition, HWI, PLC 3: ≥0.75 mm (UL 746A)
- Hot-Wire Ignition, HWI, PLC 4: ≥0.4 mm (UL 746A)
- High Amp Arc Ignition, HAI, PLC 4: ≥0.4 mm (UL 746A)
- High Voltage Arc Track Rate, PLC: 4 PLC Code (UL 746A)
- Arc Resistance, Tungsten, PLC: 6 PLC Code (ASTM D495)
Flame Characteristics
- UL Recognized Flame Rating: 94V-0 at ≥0.4 mm (UL 94)
- Additional Flame Listing: 5VA listing (datasheet description)
- ECO Conforming: Yes
Processing Parameters
- Melt Flow Rate, 337°C/6.6 kgf: 13 g/10 min (ASTM D1238)
- Mold Shrinkage, Flow, 3.2 mm: 0.5–0.7% (SABIC Method)
- Mold Shrinkage, Cross Flow, 3.2 mm: 0.5–0.7% (SABIC Method)
- Internal Mold Release: Yes
- High Flow Grade: Yes
- Enhanced Electroplatability: Yes
Certifications & Compliance
- UL Recognized: Yes
- UL Yellow Card: E207780-104152645
- UL94 Flame Class Rating: V-0 at ≥0.4 mm (UL 94)
- 5VA Listing: Yes
- ECO Conforming: Yes
- UL RTI Electrical: 105°C (UL 746B)
- UL RTI Mechanical with Impact: 105°C (UL 746B)
- UL RTI Mechanical without Impact: 105°C (UL 746B)
Use & Applications
- Automotive
- Aerospace
- Building and
- Construction
- Consumer Products
- Electrical and
- Electronics
- Healthcare and
- Hygiene
- Industrial
- Rail Mass Transportation
- Industrial packaging