ULTEM™ Resin 2210F
Plastic Granules
ULTEM™ Resin 2210F Flame Retardant 20% Glass Fiber PEI
ULTEM™ Resin 2210F is a 20% glass fiber reinforced PEI resin with enhanced flow. It offers high stiffness, 211°C HDT, UL 94V-0 flame rating at ≥0.41 mm, and strong dimensional stability for thin-wall, high-temperature injection molded parts.
Typical property data
Physical Properties
- Density: 1.42 g/cm³ (ISO 1183)
- Water Absorption, 23°C / Saturated: 1% (ISO 62-1)
- Moisture Absorption, 23°C / 50% RH: 0.55% (ISO 62)
Mechanical Properties
- Tensile Stress, Yield, Type I, 5 mm/min: 139 MPa (ASTM D638)
- Tensile Stress, Break, Type I, 5 mm/min: 140 MPa (ASTM D638)
- Tensile Strain, Yield, Type I, 5 mm/min: 2% (ASTM D638)
- Tensile Modulus, 5 mm/min: 6890 MPa (ASTM D638)
- Flexural Stress, Yield, 1.3 mm/min, 50 mm Span: 227 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm Span: 6890 MPa (ASTM D790)
- Tensile Stress, Yield, 5 mm/min: 140 MPa (ISO 527)
- Tensile Stress, Break, 5 mm/min: 140 MPa (ISO 527)
- Tensile Strain, Yield, 5 mm/min: 2% (ISO 527)
- Tensile Strain, Break, 5 mm/min: 2% (ISO 527)
- Tensile Modulus, 1 mm/min: 6800 MPa (ISO 527)
- Flexural Stress, Yield, 2 mm/min: 210 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 6500 MPa (ISO 178)
Impact Properties
- Izod Impact, Unnotched, 23°C: 475 J/m (ASTM D4812)
- Instrumented Dart Impact Total Energy, 23°C: 13 J (ASTM D3763)
- Izod Impact, Notched, 80 × 10 × 4 mm, +23°C: 5 kJ/m² (ISO 180/1A)
- Izod Impact, Notched, 80 × 10 × 4 mm, -30°C: 5 kJ/m² (ISO 180/1A)
- Charpy Impact, 23°C, V-Notch Edgewise, 80 × 10 × 4 mm, Span 62 mm: 8 kJ/m² (ISO 179/1eA)
Thermal Properties
- Glass Transition Temperature, Tg: 217°C
- Vicat Softening Temperature, Rate B/50: 226°C (ASTM D1525)
- Heat Deflection Temperature, 1.82 MPa, 6.4 mm, Unannealed: 211°C (ASTM D648)
- Vicat Softening Temperature, Rate B/50: 212°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 218°C (ISO 306)
- Relative Temperature Index, Electrical: 170°C (UL 746B)
- Relative Temperature Index, Mechanical with Impact: 170°C (UL 746B)
- Relative Temperature Index, Mechanical without Impact: 170°C (UL 746B)
Electrical Properties
- Comparative Tracking Index, CTI: PLC 4 (UL 746A)
- Hot-Wire Ignition, HWI, PLC 1: ≥3 mm (UL 746A)
- Hot-Wire Ignition, HWI, PLC 2: ≥1.5 mm (UL 746A)
- High Amp Arc Ignition, HAI, PLC 3: ≥1.5 mm (UL 746A)
- High Amp Arc Ignition, HAI, PLC 4: ≥3 mm (UL 746A)
- High Voltage Arc Track Rate: PLC 2 (UL 746A)
- Arc Resistance, Tungsten: PLC 6 (ASTM D495)
Flame Characteristics
- UL Recognized 94-5VA Flame Class Rating: ≥1.9 mm (UL 94)
- UL Recognized 94V-0 Flame Class Rating: ≥0.41 mm (UL 94)
- Flame Retardant System: Non-halogenated flame retardant
- Smoke / Toxicity Feature: Low smoke and toxicity
- PFAS Statement: No PFAS intentionally added
Processing Parameters
- Processing Technique: Injection Molding
- Flow Characteristic: Enhanced flow / high flow
- Dimensional Control Feature: Low warpage / low shrinkage
- Processing Advantage: Good processability
Use & Applications
- Thin-wall injection molded parts