ULTEM™ Resin 2210GCR3
Plastic Granules
ULTEM™ Resin 2210GCR3 Enhanced-flow 20% Glass Fiber Reinforced
ULTEM™ Resin 2210GCR3 is a 20% glass fiber reinforced PEI resin with 30% PCR and bio-based polyetherimide content. It delivers high stiffness, enhanced flow, low warpage, high heat resistance, and dimensional stability for precision injection molded components.
Associated Documents
TDS - Global Data Sheet
Typical property data
Physical Properties
- Specific Gravity: 1.42 (ASTM D792)
- Density: 1.42 g/cm³ (ISO 1183)
- Melt Flow Rate, 337°C / 6.7 kgf: 10 g/10 min (ASTM D1238)
- Melt Flow Rate, 350°C / 2.16 kgf: 6.1 g/10 min (ASTM D1238)
- Water Absorption, 23°C / 24 hrs: 0.19% (ASTM D570)
- Moisture Absorption, 23°C / 50% RH / 24 hrs: 0.06% (ISO 62-4)
- Mold Shrinkage, Flow: 0.33% (SABIC method)
- Mold Shrinkage, Cross Flow: 0.59% (SABIC method)
Mechanical Properties
- Tensile Stress at Break, Type I, 50 mm/min: 143 MPa (ASTM D638)
- Tensile Strain at Break, Type I, 50 mm/min: 4% (ASTM D638)
- Tensile Modulus, 5 mm/min: 7040 MPa (ASTM D638)
- Flexural Strength, 1.3 mm/min, 50 mm span: 231 MPa (ASTM D790)
- Flexural Modulus, 1.3 mm/min, 50 mm span: 7072 MPa (ASTM D790)
- Tensile Stress at Break, 50 mm/min: 148 MPa (ISO 527)
- Tensile Strain at Break, 50 mm/min: 3.6% (ISO 527)
- Tensile Modulus, 1 mm/min: 7020 MPa (ISO 527)
- Flexural Strength, 2 mm/min: 227 MPa (ISO 178)
- Flexural Modulus, 2 mm/min: 7030 MPa (ISO 178)
Impact Properties
- Izod Impact, Notched, 23°C: 69 J/m (ASTM D256)
- Izod Impact, Unnotched, 23°C: 544 J/m (ASTM D4812)
- Izod Impact, Notched, 80 × 10 × 4 mm, 23°C: 9 kJ/m² (ISO 180/1A)
- Izod Impact, Unnotched, 80 × 10 × 4 mm, 23°C: 35 kJ/m² (ISO 180/1U)
- Charpy Impact, V-Notch Edgewise, 23°C: 9 kJ/m² (ISO 179/1eA)
- Charpy Impact, Unnotched Edgewise, 23°C: 45 kJ/m² (ISO 179/1eU)
Thermal Properties
- Heat Deflection Temperature, 0.45 MPa, 3.2 mm, Unannealed: 211°C (ASTM D648)
- Heat Deflection Temperature, 1.82 MPa, 3.2 mm, Unannealed: 208°C (ASTM D648)
- HDT/Bf, 0.45 MPa, Flatwise, 80 × 10 × 4 mm: 214°C (ISO 75/Bf)
- HDT/Af, 1.8 MPa, Flatwise, 80 × 10 × 4 mm: 208°C (ISO 75/Af)
- Coefficient of Thermal Expansion, Flow, 23°C to 150°C: 2.1E-05 1/°C (ASTM E831)
- Coefficient of Thermal Expansion, Cross Flow, 23°C to 150°C: 5.0E-05 1/°C (ASTM E831)
- Coefficient of Thermal Expansion, Flow, 23°C to 150°C: 2.0E-05 1/°C (ISO 11359-2)
- Coefficient of Thermal Expansion, Cross Flow, 23°C to 150°C: 5.0E-05 1/°C (ISO 11359-2)
- Vicat Softening Temperature, Rate B/50: 215°C (ASTM D1525)
- Vicat Softening Temperature, Rate B/120: 215°C (ASTM D1525)
- Vicat Softening Temperature, Rate B/50: 215°C (ISO 306)
- Vicat Softening Temperature, Rate B/120: 217°C (ISO 306)
- Glass Transition Temperature, Tg: 217°C — stated in product description
Processing Parameters
- Processing Technique: Injection Molding
- Drying Temperature: 140–150°C
- Drying Time: 4–6 hrs
- Cumulative Drying Time: 24 hrs
- Maximum Moisture Content: 0.02%
- Melt Temperature: 350–400°C
- Nozzle Temperature: 345–400°C
- Front Zone 3 Temperature: 345–400°C
- Middle Zone 2 Temperature: 345–400°C
- Rear Zone 1 Temperature: 330–400°C
- Mold Temperature: 135–165°C
- Back Pressure: 0.3–0.7 MPa
- Screw Speed: 40–70 rpm
- Shot to Cylinder Size: 40–60%
- Vent Depth: 0.025–0.076 mm
Use & Applications
- for precision injection molded components