YUNGSOX® PP 2100M Homopolymer
Plastic Granules
YUNGSOX® PP 2100M Homopolymer
YUNGSOX® PP 2100M is a HOMOPOLYMER PP resin for CPP film and aluminum metallized cast film. It offers clear film quality and stable lamination performance. Characteristics: Good metallizing properties, Excellent transparency, Excellent laminate performance.
Associated Documents
TDS - Data Sheet
PL JCII Certification
SDS - PPH
BPA - PPH
Haolgen - PPH
PAHs - PPH
REACH SVHC - PPH
RoHS - PPH
EN71-3 - PPH
EU10-2011 - PPH
FDA - PPH
GB4806.6 - PPH
Typical property data
Physical Properties
- Melt Index: 7 g/10 min (ISO 1133 / ASTM D-1238)
- Density: 0.90 g/cm³ (ISO 1183 / ASTM D792)
Mechanical Properties
- Tensile Strength at Yield: 350 kg/cm² / 34 MPa (ISO 527 / ASTM D-638)
- Tensile Elongation at Break: 500% (ISO 527 / ASTM D-638)
- Rockwell Hardness: 107 R scale (ISO 2039 / ASTM D-785)
- Flexural Modulus: 14,000 kg/cm² / 1,373 MPa (ISO 178 / ASTM D-790)
- IZOD Impact Strength at 23°C: 4.0 kg·cm/cm Notch / 39 J/m (ISO 180 / ASTM D-256)
Thermal Properties
- Melting Point: 165°C (DSC)
- Heat Deflection Temperature: 115°C (ISO 75 / ASTM D-648)
- Vicat Softening Temperature: 155°C (ISO 306)
Optical Properties
- Haze, 30 μm Film: < 0.5% (FPC Method)
- Transparency: Excellent transparency
- Metallizing Performance: Good metallizing properties
- Lamination Performance: Excellent laminates
Processing Parameters
- Mold Shrinkage: 1.3–1.7% (FPC Method)
- Melt Index: 7 g/10 min (ISO 1133 / ASTM D-1238)
Certifications & Compliance
- FDA Food Contact Compliance: FDA 21 CFR 177.1520 requirements for direct food contact
- Regulation Reference: FDA Code of Federal Regulations, 21 CFR 177.1520
Use & Applications
- CPP film
- Aluminum metallized cast film