YUNGSOX® PP 3300N Impact Copolymer
Plastic Granules
YUNGSOX® PP 3300N Impact Copolymer High Fluidity
YUNGSOX® PP 3300N is a high-flow impact copolymer PP resin for large molded parts and thin-wall products. It delivers 30 g/10 min melt index, 137 J/m IZOD impact at 23°C, uniform 1.3–1.7% shrinkage, and balanced stiffness.
Associated Documents
TDS - Data Sheet
SDS - PP Impact Copolymer
BPA - PP Impact Copolymer
Haolgen - PP Impact Copolymer
PAHs - PP Impact Copolymer
REACH SVHC - PP Impact Copolymer
RoHS - PP Impact Copolymer
EN71-3 - PP Impact Copolymer
EU10-2011 - PP Impact Copolymer
FDA - PP Impact Copolymer
GB4806.6 - PP Impact Copolymer
Typical property data
Physical Properties
- Melt Index: 30 g/10 min (ISO 1133 / ASTM D-1238)
- Density: 0.90 g/cm³ (ISO 1183 / ASTM D792)
- Mold Shrinkage: 1.3–1.7% (FPC Method)
Mechanical Properties
- Tensile Strength at Yield: 260 kg/cm² / 27 MPa (ISO 527 / ASTM D-638)
- Tensile Elongation at Break: 100% (ISO 527 / ASTM D-638)
- Rockwell Hardness: 95 R Scale (ISO 2039 / ASTM D-785)
- Flexural Modulus: 10,500 kg/cm² / 1,030 MPa (ISO 178 / ASTM D-790)
- IZOD Impact Strength at 23°C: 14 kg·cm/cm Notch / 137 J/m (ISO 180 / ASTM D-256)
- IZOD Impact Strength at -20°C: 8 kg·cm/cm Notch / 78 J/m (ISO 180 / ASTM D-256)
Thermal Properties
- Heat Deflection Temperature: 105°C (ISO 75 / ASTM D-648)
- Vicat Softening Temperature: 140°C (ISO 306)
Processing Parameters
- Melt Index: 30 g/10 min (ISO 1133 / ASTM D-1238)
- Mold Shrinkage: 1.3–1.7% (FPC Method)
- Processing Characteristic: High fluidity
- Shrinkage Characteristic: Uniform shrinkage
Use & Applications
- Larger automotive parts
- Electric appliance parts
- Washing machine parts
- Tool boxes
- Storage boxes
- Thin wall products