YUNGSOX® PP 3504 Impact Copolymer
Plastic Granules
YUNGSOX® PP 3504 Impact Copolymer
YUNGSOX® PP 3504 is a high-flow impact copolymer PP resin for large parts and thin-wall molding. It offers 55 g/10 min melt flow, 1,275 MPa flexural modulus, 125°C HDT, and FDA 21 CFR 177.1520 compliance for reliable B2B applications.
Associated Documents
TDS - Data Sheet
PL JCII Certification
SDS - PP Impact Copolymer
BPA - PP Impact Copolymer
Haolgen - PP Impact Copolymer
PAHs - PP Impact Copolymer
REACH SVHC - PP Impact Copolymer
RoHS - PP Impact Copolymer
EN71-3 - PP Impact Copolymer
EU10-2011 - PP Impact Copolymer
FDA - PP Impact Copolymer
GB4806.6 - PP Impact Copolymer
Typical property data
Physical Properties
- Melt Index: 55 g/10 min (ISO 1133 / ASTM D-1238)
- Density: 0.90 g/cm³ (ISO 1183 / ASTM D792)
- Mold Shrinkage: 1.3–1.7% (FPC Method)
Mechanical Properties
- Tensile Strength at Yield: 270 kg/cm² / 26 MPa (ISO 527 / ASTM D-638)
- Tensile Elongation at Break: 100% (ISO 527 / ASTM D-638)
- Flexural Modulus: 13,000 kg/cm² / 1,275 MPa (ISO 178 / ASTM D-790)
- Rockwell Hardness: 100 R scale (ISO 2039 / ASTM D-785)
- IZOD Impact Strength at 23°C: 8.5 kg·cm/cm notch / 83 J/m (ISO 180 / ASTM D-256)
- IZOD Impact Strength at -20°C: 4 kg·cm/cm notch / 39 J/m (ISO 180 / ASTM D-256)
Thermal Properties
- Heat Deflection Temperature: 125°C (ISO 75 / ASTM D-648)
- Vicat Softening Temperature: 155°C (ISO 306)
Processing Parameters
- Flow Characteristic: Superhigh fluidity
- Melt Index: 55 g/10 min (ISO 1133 / ASTM D-1238)
- Mold Shrinkage: 1.3–1.7% (FPC Method)
- Recommended Application Processing: Injection molding
Use & Applications
- Larger automotive parts
- Electric appliance parts
- Washing machine parts
- Storage boxes
- Thin-wall products