YUNGSOX® PP 5018T Random Copolymer
Plastic Granules
YUNGSOX® PP 5018T Random Copolymer
YUNGSOX® PP 5018T is a random copolymer PP resin for clear blow-molded packaging. It offers high transparency, good luster, 1.7 g/10 min melt index, 0.90 g/cm³ density, and FDA 21 CFR 177.1520 food-contact compliance for juice bottles and clear portfolios.
Associated Documents
TDS - Data Sheet
JCII PL Test
PPR copolymer - Halogen
PPR copolymer - PAHs
PPR copolymer - REACH SVHC
PPR copolymer - RoHS
PPR copolymer - BPA
PPR copolymer - EN71-3
PPR copolymer - EU10-2011
PPR copolymer - FDA
PP Terpolymer - EU10-2011
Typical property data
Physical Properties
- Melt Index: 1.7 g/10 min (ISO 1133 / ASTM D-1238)
- Density: 0.90 g/cm³ (ISO 1183 / ASTM D792)
- Mold Shrinkage: 1.3–1.7% (FPC Method)
Mechanical Properties
- Tensile Strength at Yield: 300 kg/cm² / 29 MPa (ISO 527 / ASTM D-638)
- Tensile Elongation at Break: 400% (ISO 527 / ASTM D-638)
- Rockwell Hardness: 98 R Scale (ISO 2039 / ASTM D-785)
- Flexural Modulus: 10,500 kg/cm² / 1,030 MPa (ISO 178 / ASTM D-790)
- IZOD Impact Strength at 23°C: 15 kg·cm/cm Notch / 147 J/m (ISO 180 / ASTM D-256)
Thermal Properties
- Melting Point: 146°C (DSC)
- Heat Deflection Temperature: 95°C (ISO 75 / ASTM D-648)
- Vicat Softening Temperature: 125°C (ISO 306)
Optical Properties
- High Transparency
- Good Luster
Processing Parameters
- Recommended Processing: Blow molding
- Melt Index for Processing Reference: 1.7 g/10 min (ISO 1133 / ASTM D-1238)
- Mold Shrinkage for Tooling Reference: 1.3–1.7% (FPC Method)
Certifications & Compliance
- FDA Food Contact Compliance: FDA 21 CFR 177.1520
Use & Applications
- Blow molding
- Juice bottle
- Transparency portfolio