YUNGSOX® PP 5020 Random Copolymer
Plastic Granules
YUNGSOX® PP 5020 Random Copolymer
YUNGSOX® PP 5020 is a random copolymer PP resin for shrink film. It offers low heat seal temperature, good softness, and low haze below 1.0% at 30 μm. With 500% elongation and FDA 21 CFR 177.1520 compliance, it supports clear food-contact film packaging.
Associated Documents
TDS - Data Sheet
PPR copolymer - Halogen
PPR copolymer - PAHs
PPR copolymer - REACH SVHC
PPR copolymer - RoHS
PPR copolymer - BPA
PPR copolymer - EN71-3
PPR copolymer - EU10-2011
PPR copolymer - FDA
PP Terpolymer - EU10-2011
Typical property data
Physical Properties
- Melt Index: 3 g/10 min (ISO 1133 / ASTM D-1238)
- Density: 0.90 g/cm³ (ISO 1183 / ASTM D792)
- Mold Shrinkage: 1.3–1.7% (FPC Method)
Mechanical Properties
- Tensile Strength at Yield: 200 kg/cm² / 20 MPa (ISO 527 / ASTM D-638)
- Tensile Elongation at Break: 500% (ISO 527 / ASTM D-638)
- Flexural Modulus: 5,000 kg/cm² / 490 MPa (ISO 178 / ASTM D-790)
- IZOD Impact Strength, Notched, 23°C: 12 kg·cm/cm / 118 J/m (ISO 180 / ASTM D-256)
Thermal Properties
- Melting Point: 133°C (DSC)
- Heat Deflection Temperature: 75°C (ISO 75 / ASTM D-648)
- Vicat Softening Temperature: 110°C (ISO 306)
Optical Properties
- Haze, 30 μm Film: < 1.0% (FPC Method)
Processing Performance
- Low Heat-Sealing Performance
- Good Material Softness
- Melt Flow Suitability: 3 g/10 min melt index (ISO 1133 / ASTM D-1238)
- Dimensional Control Reference: 1.3–1.7% mold shrinkage (FPC Method)
Certifications & Compliance
- FDA Food Contact Compliance: FDA 21 CFR 177.1520 requirements for direct food contact
Use & Applications
- Shrink film