YUNGSOX® PP HS9020 Homopolymer
Plastic Granules
YUNGSOX® PP HS9020 Homopolymer
YUNGSOX® PP HS9020 is a high melt strength Homopolymer PP resin for foam extrusion and thermoforming. It offers stable melt strength, high rigidity, and high crystallization performance.
Associated Documents
TDS - Data Sheet
SDS - PPH
BPA - PPH
Haolgen - PPH
PAHs - PPH
REACH SVHC - PPH
RoHS - PPH
EN71-3 - PPH
EU10-2011 - PPH
FDA - PPH
GB4806.6 - PPH
Typical property data
Physical Properties
- Melt Index: 1.6 g/10 min (ISO 1133 / ASTM D-1238)
- Density: 0.90 g/cm³ (ISO 1183 / ASTM D792)
- Mold Shrinkage: 2.1–2.5% (FPC Method)
- Melt Strength: 30 cN (ISO 16790)
Mechanical Properties
- Tensile Strength at Yield: 400 kg/cm² / 39 MPa (ISO 527 / ASTM D-638)
- Tensile Elongation at Break: 12% (ISO 527 / ASTM D-638)
- Rockwell Hardness: 100 R scale (ISO 2039 / ASTM D-785)
- Flexural Modulus: 20,000 kg/cm² / 1,961 MPa (ISO 178 / ASTM D-790)
- IZOD Impact Strength, Notched, 23°C: 3.0 kg·cm/cm / 29 J/m (ISO 180 / ASTM D-256)
Thermal Properties
- Melting Point: 165°C (ISO 11357)
- Crystallization Point: 125°C (ISO 11357)
- Heat Deflection Temperature: 132°C (ISO 75 / ASTM D-648)
- Vicat Softening Temperature: 153°C (ISO 306)
Processing Parameters
- Recommended Processing: Foam extrusion
- Recommended Processing: Thermoforming
- Key Processing Capability: High melt strength, 30 cN (ISO 16790)
- Flow Behavior: Low Melt Index, 1.6 g/10 min (ISO 1133 / ASTM D-1238)
- Dimensional Change After Molding: 2.1–2.5% Mold Shrinkage (FPC Method)
Use & Applications
- Foam extrusion
- Thermoforming