Zhenjiang Chimei Polylac® D-1200
Plastic Granules
Polylac® D-1200 Flame Retardant Grade Standard Flow
Polylac® D-1200 is a flame-retardant-grade ABS resin designed for durable, safe, and efficient applications. With standard flow and excellent flame ratings (1.5mm V-2, 2.5mm V-0, 2.5mm 5VB, 3.0mm 5VA), it is TBBA-based and perfect for high-performance industrial needs.
Typical property data
Physical Properties
- Melt Flow Rate (MFR):
- 4.5 cm³/10 min (ISO 1133, 200°C/5 kg)
- 47 cm³/10 min (ISO 1133, 220°C/10 kg)
- Density: 1.17 g/cm³ (ISO 1183, 23°C)
- Hardness: R-102 (ASTM D785)
Mechanical Properties
- Tensile Strength: 38 MPa (ISO 527, 50 mm/min)
- Elongation: 20% (ISO 527, 50 mm/min)
- Flexural Strength: 65 MPa (ISO 178, 2 mm/min)
- Flexural Modulus: 2.2 GPa (ISO 178, 2 mm/min)
Impact Properties
- IZOD Impact Strength: 19 kJ/m² (ISO 180, 4 mm/23°C)
- Charpy Impact Strength: 20 kJ/m² (ISO 179, 4 mm/23°C)
Thermal Properties
- Vicat Softening Point: 92°C (ISO 306, 10 N, 50°C/hr)
- Heat Deflection Temperature (HDT):
- Annealed: 85°C (ISO 75-2, 1.8 MPa)
- Unannealed: 72°C (ISO 75-2, 1.8 MPa)
Flame Characteristics
- UL Rating: V-0 at 2.5 mm (File No. E194560)
Use & Applications
- Set-top boxes
- Power switch panels
- Power sockets
- Car batteries
- Cash register housings
- Light boxes
- DVD players
- Car audio control panels
Features & Benefits
1. Superior Flame Resistance for Safety
Polylac® D-1200 meets stringent UL ratings, including V-0 at 2.5mm, ensuring excellent fire safety in critical applications.
2. High Mechanical Strength & Durability
With 38 MPa tensile strength and 2.2 GPa flexural modulus, this resin offers toughness and reliability under load.
3. Thermal Stability for Performance
Able to withstand up to 85°C (annealed), Polylac® D-1200 remains stable under high temperatures, ensuring lasting functionality.