Zhenjiang Chimei Polylac® D-1400
Plastic Granules
Polylac® D-1400 Flame Retardant Grade 3.0mm V0 (TBBA Series)
Polylac® D-1400 is an advanced flame-retardant ABS plastic resin (3.0mm V-0, TBBA series) designed for high-performance durability and thermal stability. With excellent mechanical strength, impact resistance, and moldability, it caters perfectly to stringent industrial demands.
Typical property data
Physical Properties
- Melt Flow Rate (MFR):
- 4.0 cm³/10min (ISO 1133, 200℃, 5 kg)
- 42 cm³/10min (ISO 1133, 220℃, 10 kg)
- Density: 1.15 g/cm³ (ISO 1183, 23℃)
- Hardness: R-103 (ASTM D785)
Mechanical Properties
- Tensile Strength: 40 MPa (ISO 527, 50 mm/min)
- Elongation: 25% (ISO 527, 50 mm/min)
- Flexural Strength: 64 MPa (ISO 178, 2 mm/min)
- Flexural Modulus: 2.2 GPa (ISO 178, 2 mm/min)
Impact Properties
- Izod Impact Strength: 20 kJ/m² (ISO 180, 4 mm/23℃)
- Charpy Impact Strength: 22 kJ/m² (ISO 179, 4 mm/23℃)
Thermal Properties
- Softening Point: 94℃ (ISO 306, 10N, 50℃/hr)
- Heat Deflection Temperature (HDT):
- 85℃, annealed (ISO 75-2, 1.8 MPa)
- 75℃, unannealed (ISO 75-2, 1.8 MPa)
Flame Characteristics
- Flame Retardancy Ratings (UL 94):
- 2.0 mm: V-2
- 3.0 mm: V-0
Use & Applications
- Set-top boxes
- Power switch panels
- Power outlets
- Car batteries
- Cash register housings
- Light boxes
- DVD players
- Car audio control panels
Features & Benefits
1. Exceptional Flame Retardancy
Polylac® D-1400 achieves UL 94 V-0 at 3.0 mm, ensuring reliable fire safety for critical applications.
2. Superior Mechanical Strength
With 40 MPa tensile strength and 2.2 GPa flexural modulus, it provides outstanding durability for structural components.
3. Efficient Injection Moldability
Its melt flow rate of 42 cm³/10min allows smooth processing, reducing material waste in complex industrial designs.