Zhenjiang Chimei Polylac® D-2200
Plastic Granules
Polylac® D-2200 Heat-Resistant Grade High Impact Strength
Polylac® D-2200 is a heat-resistant, high-impact strength ABS resin designed to meet the rigorous demands of modern industries. It combines durability, flexibility, and thermal stability, making it essential for automotive, electronics, and consumer goods production.
Typical property data
Physical Properties
- Melt Flow Index (MFI):
- 11 cm³/10 min at 220°C, 10kg (ISO 1133)
- Density: 1.04 g/cm³ (ISO 1183)
- Hardness: R-115 (ASTM D785)
Mechanical Properties
- Tensile Strength: 42 MPa at 50 mm/min (ISO 527)
- Elongation at Break: 30% at 50 mm/min (ISO 527)
- Flexural Strength: 68 MPa at 2 mm/min (ISO 178)
- Flexural Modulus: 2.3 GPa at 2 mm/min (ISO 178)
Impact Properties
- Izod Impact Strength: 17 kJ/m² at 4 mm/23°C (ISO 180)
- Charpy Impact Strength: 18 kJ/m² at 4 mm/23°C (ISO 179)
Thermal Properties
- Vicat Softening Point: 112°C, 10N, 50°C/hr (ISO 306)
- Heat Deflection Temperature (HDT):
- Annealed: 104°C at 1.8 MPa (ISO 75-2)
- Unannealed: 86°C at 1.8 MPa (ISO 75-2)
Flame Characteristics
- Flammability Rating: HB at 1.5 mm (File No. E194560; UL & C-UL)
Injection Molding
- Shrinkage: 0.3–0.6% (ISO 294-4)
Use & Applications
- Automotive-related products
- Electronics
- Electrical appliances
Features & Benefits
1. High Impact Strength & Durability
Polylac® D-2200 excels in toughness, ensuring products withstand impacts and daily wear for long-lasting performance.
2. Superior Heat Resistance
With a heat deflection temperature of up to 104°C, this ABS resin thrives in high-temperature environments.
3. Precision Moldability
A low shrinkage rate of 0.3–0.6% delivers precise parts, reducing waste and streamlining injection molding processes.