Polylac® PA-717CK General Grade High impact Strength
Polylac® PA-717CK is a general-grade ABS resin offering high impact strength, excellent thermal stability, and efficient processability. Designed for versatile applications, it ensures durability, safety (UL HB certified), and precision – ideal for automotive, electronics, and consumer goods.
Typical property data
Physical Properties
Melt Flow Rate (MFR):
- 1.2 cm³/10 min (ISO 1133, 200°C, 5 kg)
- 14 cm³/10 min (ISO 1133, 220°C, 10 kg)
- Density: 1.04 g/cm³ (ISO 1183, 23°C)
- Hardness: R-115 (ASTM D785)
Mechanical Properties
- Tensile Strength: 43 MPa (ISO 527, 50 mm/min)
- Elongation at Break: 20% (ISO 527, 50 mm/min)
- Flexural Strength: 67 MPa (ISO 178, 2 mm/min)
- Flexural Modulus: 2.3 GPa (ISO 178, 2 mm/min)
Impact Properties
- Izod Impact Strength: 25 kJ/m² (ISO 180, 4 mm/23°C)
- Charpy Impact Strength: 27 kJ/m² (ISO 179, 4 mm/23°C)
Thermal Properties
- Vicat Softening Point: 102°C (ISO 306, 10N, 50°C/hr)
- Heat Deflection Temperature (HDT):
- 97°C (1.8 MPa, annealed) (ISO 75-2)
- 82°C (1.8 MPa, unannealed) (ISO 75-2)
Flame Characteristics
- UL Flammability: HB (1.5 mm, File No. E194560)
Use & Applications
- Kitchenware
- Toilet Seats
- Washing Machines & Vacuum Cleaner Housings
- Tool Handles & Accessories
Features & Benefits
1. High Impact Strength
Polylac® PA-717CK resists cracking and breaking, ensuring reliable performance for demanding industrial applications.
2. Outstanding Thermal Stability
With a heat deflection temperature of up to 97°C, it maintains form and function in high-heat environments.
3. Superior Processability
Its excellent melt flow rate allows for efficient injection molding, reducing production downtime and material waste.