Zhenjiang Chimei Wonderloy® PC-330K
Plastic Granules
Wonderloy® PC-330K PC/ABS Low-odor Grade Low VOC
Wonderloy® PC-330K is a high-performance PC/ABS plastic resin featuring low odor and low VOC emissions. Designed for high-flow processing, it offers outstanding mechanical strength and impact resistance. Ideal for industries prioritizing durability and precision.
Typical property data
Physical Properties
- Density: 1.07 g/cm³ (ISO 1183, 23°C)
- Melt Flow Rate (MFR): 34 cm³/10min (ISO 1133, 260°C, 5kg)
Mechanical Properties
- Tensile Strength: 47 MPa (ISO 527, 50 mm/min)
- Tensile Elongation at Break: 50% (ISO 527, 50 mm/min)
- Flexural Strength: 70 MPa (ISO 178, 2 mm/min)
- Flexural Modulus: 2.1 GPa (ISO 178, 2 mm/min)
- Hardness: 108 HRR (ASTM D785, 1/2”)
Impact Properties
- IZOD Notched Impact Strength: 35 kJ/m² (ISO 180, 3.2mm, 23°C)
- Charpy Impact Strength: 36 kJ/m² (ISO 179, 3.2mm, 23°C)
Thermal Properties
- Vicat Softening Temperature:
- 114°C (ISO 306, 10N, 50°C/hr)
- 105°C (ISO 306, 50N, 50°C/hr)
- Heat Deflection Temperature (HDT):
- 86°C at 1.8 MPa (ISO 75-2, unannealed)
- 105°C at 0.46 MPa (ISO 75-2, unannealed)
Flame Characteristics
- Flammability Rating: UL 94 HB, 1.5mm (File No. E194560)
Use & Applications
- Automotive interior components
- Electronic product housings
- General molded parts
Features & Benefits
1. Superior Strength and Flexibility
It offers 47 MPa tensile strength and 50% elongation, ensuring durability and flexibility.
2. Exceptional Impact Resistance
With 35 kJ/m² IZOD impact strength, it provides reliable protection for products in impact-prone environments.
3. High Heat Resistance
It withstands up to 114°C (Vicat softening temperature), making it ideal for high-temperature applications like automotive and electronics.