ZPC ZA0210H ABS Resin
Plastic Granules
ZPC ZA0210H General ABS High Gloss High Stiffness
ZPC ABS ZA0210H is a high-performance black ABS plastic resin offering exceptional high gloss, remarkable stiffness, and excellent processability. Perfect for manufacturing durable, aesthetically superior components in home appliances, electronics, and consumer goods.
Associated Documents
TDS - Data Sheet
Typical property data
Physical Properties
- Mass Density: 1.04 g/cm³ (GB/T 1033.1, 23 ℃)
- Melt Flow Rate (MFR): 20 g/10 min (GB/T 3682.1, 220 ℃/10 kg)
- Mold Shrinkage: 0.4–0.7% (GB/T 17037.4)
- Rockwell Hardness (R-Scale): 109 (GB/T 3398.2)
Mechanical Properties
- Tensile Strength: 44 MPa (GB/T 1040.2, 50 mm/min)
- Flexural Strength: 68 MPa (GB/T 9341, 2 mm/min)
- Flexural Modulus: 2.4 GPa (GB/T 9341, 2 mm/min)
- Charpy Impact Strength (Notched, 23 ℃): 22 KJ/m² (GB/T 1043.1)
Thermal Properties
- Heat Distortion Temperature (HDT, 1.8 MPa, unannealed): 83 ℃ (GB/T 1634.2)
- Vicat Softening Temperature (50 N, 50 ℃/hr): 95 ℃ (GB/T 1633)
Flame Characteristics
- Flame Rating: HB at 1.5 mm (UL-94)
Processing Parameters
- Drying Temperature: 75–85 ℃
- Drying Time: 2–4 hours
- Barrel Temperature: 180–220 ℃
- Nozzle Temperature: 200–220 ℃
- Mold Temperature: 40–70 ℃
- Back Pressure: 10–30 bar
- Screw Speed: 30–60 rpm
Use & Applications
- Home appliances
- Electronic and electrical products
Features & Benefits
1. High Gloss and Stiffness
ZPC ABS ZA0210H is ideal for applications needing surface shine and mechanical strength.
2. Versatile Usability
Suitable for home appliances, electronics, and electrical products.
3. Efficient Processing
Excellent mold shrinkage control (0.4–0.7%) and high fluidity (MFR: 20 g/10 min).
4. Thermal Durability
With its Vicat Softening Temperature of 95 ℃ and Heat Distortion Temperature of 83 ℃, it offers reliable performance in warm environments.