ZPC ZA0211 ABS Resin
Plastic Granules
ZPC ZA0211 General ABS High Gloss High Impact
ZPC ABS ZA0211 is a specialized ABS plastic resin offering unmatched high gloss, superior impact resistance, and exceptional processability. It’s the ideal solution for manufacturing durable and visually appealing consumer goods, electronics, and appliances.
Associated Documents
TDS - Data Sheet
Typical property data
Physical Properties
- Mass Density: 1.035 g/cm³ (GB/T 1033.1, 23°C)
- Melt Flow Rate (MFR): 20 g/10min (GB/T 3682.1, 220°C/10kg)
- Mold Shrinkage: 0.4%–0.7% (GB/T 17037.4)
- Rockwell Hardness: 109 R-scale (GB/T 3398.2)
Mechanical Properties
- Tensile Strength: 43 MPa (GB/T 1040.2, 50 mm/min)
- Flexural Strength: 68 MPa (GB/T 9341, 2 mm/min)
- Flexural Modulus: 2.4 GPa (GB/T 9341, 2 mm/min)
- Charpy Impact Strength (Notched): 23 kJ/m² (GB/T 1043.1, 23°C)
Thermal Properties
- Heat Distortion Temperature (HDT): 83°C at 1.8 MPa (unannealed) (GB/T 1634.2)
- Vicat Softening Temperature: 95°C (GB/T 1633, 50N, 50°C/h)
Flame Characteristics
- UL-94 Flammability Rating: HB (1.5 mm thickness)
Processing Parameters
- Drying Temperature: 75–85°C
- Drying Time: 2–4 hours
- Barrel Temperature: 180–220°C
- Nozzle Temperature: 200–220°C
- Mold Temperature: 40–70°C
- Back Pressure: 10–30 bar
- Screw Speed: 30–60 rpm
Use & Applications
- Home appliances
- Electronic and electrical products
Features & Benefits
1. Industry-Leading High Gloss Finish
It achieves premium gloss with a Rockwell Hardness of 109 (R-scale), enhancing product surfaces.
2. Superior Impact Resistance
With a Charpy Impact Strength of 23 kJ/m² (Notched, 23°C), ZA0211 ensures exceptional durability and resilience in high-stress applications.
3. Reliable Heat Resistance and Stability
With a Vicat Softening Temperature of 95°C and a Heat Distortion Temperature of 83°C (1.8 MPa, unannealed). Low mold shrinkage (0.4%–0.7%) ensures consistent precision.