WONDERLOY® PC-365 High-Impact PC/ABS Resin Material
WONDERLOY PC-365 is a high-heat, high-impact PC/ABS resin ideal for demanding applications. It offers excellent heat resistance up to 138°C, exceptional impact strength even at low temperatures, and good processability. With a UL94 HB rating at 1.5mm, it’s suitable for various uses requiring durability and heat resistance. Perfect for tough, long-lasting parts.
- Application: Automotive interior parts, consumer electronics products, high-end helmets, mobile phone casings, general molding products
- Character: Balanced type, 1.5mm HB
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides. All documents are sourced directly from manufacturers.
WONDERLOY® PC-365 Datasheet
| General WONDERLOY® PC-365 | ||||
| Product Description: High heat, High impact | ||||
| Properties | ISO Test Method | Test Condition | Unit | PC-365 |
| Melt Flow Index | 1133 | 260℃×5KG | ml/10 min | 20 |
| Spiral flow | CHIMEI | 260℃,2mm, | cm | 35 |
| V:50%,P:50% | ||||
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.13 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 54 |
| 50 mm/min, break | MPa | 50 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 115 |
| Flexural Strength | 178 | 2 mm/min | MPa | 80 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 2.2 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 50 |
| -30℃, Notched | KJ/m2 | 45 | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 50 |
| -30℃, Notched | KJ/m2 | 45 | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 138 |
| 50℃/hr;5KG | ℃ | 127 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 102 |
| 1.8MPa, annealed | ℃ | – | ||
| Dielectric Constant | IEC 60250 | 1MHz | — | 3.1 |
| Volume Resistivity | IEC 60093 | — | Ohm X m | 1E+16 |
| Surface Resistivity | IEC 60093 | — | Ohm | 1E+16 |
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 8*10⁻⁵ |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.4~0.6 |
| Symbol | 1043 | – | – | >PC+ABS< |
| January 12, 2024 | ||||
WONDERLOY® PC-365 UL Product iQ
| WONDERLOY® PC-365 | UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) “WONDERLOY”, furnished as pellets |
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 4 | |
| 3.0 mm | PLC 4 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 2 | |
| 3.0 mm | PLC 2 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746A |
| Dielectric Strength | 32 kV/mm | ASTM D149 |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | |
| Volume Resistivity | 1.0E+14 ohms·cm | ASTM D257/IEC 60093 |
| High Voltage, Low Current Arc Resistance | PLC 5 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| PHYSICAL PROPERTIES | VALUE | TEST METHOD |
| Dimensional Change | 0.0 % | ASTM D1042/ISO 2796 |
| Report Date: 2016-09-13 | ||