Polylac® PA-704 LRP Low Monomer Residue Medical ABS
With its excellent compliance standards and impressive mechanical properties, Polylac PA-704 LRP is set to become a key material in the medical industry. Whether it’s making sturdy surgical tools or reliable diagnostic equipment, this Medical ABS resin is a safe and dependable choice for medical applications.
- Character: Low monomer residue (EU 10/2011 Certification), comply with Bio-compatibility test (ISO10993)
- Application: Medical Application
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.
Polylac® PA-704 LRP Datasheet
| Medical ABS POLYLAC® PA-704 LRP | ||||
| Product Description: Low residual monomer, medical application | ||||
| Properties | ISO Test Method | Test Condition | Unit | PA-704 LRP |
| Melt Flow Index | 1133 | 220℃×10KG | ml/10 min | 17 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.05 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 47 |
| 50 mm/min, break | MPa | 34 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 70 |
| Flexural Strength | 178 | 2 mm/min | MPa | 76 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 2.2 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 20 |
| -30℃, Notched | KJ/m2 | 9 | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 21 |
| Charpy -30℃, Notched | KJ/m2 | 10 | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 104 |
| 50℃/hr;5KG | ℃ | 100 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 83 |
| 1.8MPa, annealed | ℃ | 98 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 8.6 x 10-5 |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.4~0.7 |
| Symbol | 1043 | – | – | >ABS< |
| July 22, 2021 | ||||
Polylac® PA-704 LRP UL Product iQ
| POLYLAC® PA-704 LRP UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets |
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 4 | |
| 3.0 mm | PLC 3 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 0 | |
| 3.0 mm | PLC 0 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746A |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | |
| High Voltage, Low Current Arc Resistance | PLC 7 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 85 °C | |
| 3.0 mm | 85 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 80 °C | |
| 3.0 mm | 80 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 85 °C | |
| 3.0 mm | 85 °C | |