Chimei Polylac PA-727 Molding Electroplating ABS Resin

Polylac® PA-727 Super Impact General ABS Resin

POLYLAC PA-727 is an ABS resin from Chi Mei known for its ultra-high impact resistance and excellent electroplating capabilities. It is ideal for applications in which strength and durability are paramount, such as in the production of pipes, appliances, and large containers. For detailed properties, please refer to the polylac pa 727 datasheet.

Application: General molding for decorative accessories, audio equipment panels, tire covers, toiletries, clock casings
Character: Ultra-high impact resistance

ABS Resin

Chimei POLYLAC® ABS Resin

Download

Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.

ISO TDS Download

ASTM TDS Download

MSDS Download

UL Product iQ Download

RoHS Download

REACH SVHC Download

Process Guide Download

Ultra-High Impact Resistance

This pa 727 abs resin offers superior impact strength with an Izod impact strength of 24 KJ/m2 at 23°C. It ensures that products made with abs polylac pa-727 can withstand substantial mechanical stress without breaking, making it a reliable choice for demanding applications.

Versatile Applications

Chi Mei polylac pa 727 is perfect for a variety of uses, including pipe materials, home appliances, and large containers. Its durability and strength make it suitable for items that need to handle heavier loads and endure wear and tear.

Excellent Thermal Stability

Polylac pa 727 maintains stability under high temperatures, with a Vicat softening temperature of 105°C. This ensures that the resin does not deform or lose its form when subjected to heat. Additionally, its flammability rating of 1.5mm HB under UL-94 standards guarantees that it meets important safety requirements.

Polylac® PA-727 Datasheet

Electroplating ABS POLYLAC® PA-727
Product Description: Electroplating
Properties	ISO Test Method	Test Condition	Unit	PA-727
Melt Flow Index	1133	220℃×10KG	ml/10 min	19
Mass Density	1183	23 ℃	g/cm3	1.05
Tensile Strength	527	50 mm/min, yield	MPa	46
Tensile Strength	527	50 mm/min, break	MPa	34
Tensile Elongation	527	50 mm/min	%	50
Flexural Strength	178	2 mm/min	MPa	71
Flexural Modulus	178	2 mm/min	GPa	2
Izod Impact Strength	180/1A	23℃, Notched	KJ/m2	24
Izod Impact Strength	180/1A	-30℃, Notched	KJ/m2	11
Charpy Impact Strength	179	23℃, Notched	KJ/m2	25
Charpy Impact Strength	179	-30℃, Notched	KJ/m2	12
Vicat Softening Temp.	306	50℃/hr;1KG	℃	105
Vicat Softening Temp.	306	50℃/hr;5KG	℃	98
Heat Distortion Temp.	75/A	1.8MPa, unannealed	℃	83
Heat Distortion Temp.	75/A	1.8MPa, annealed	℃	100
Coefficient of Linear Thermal Expansion	11359	–	–	8.8 x 10-5
Flammability	–	UL-94	–	1.5mm HB
Mold Shrinkage	294-4	–	%	0.4~0.7
Symbol	1043	–	–	>ABS<
				March 11, 2024

Polylac® PA-727 UL Product iQ

POLYLAC® PA-727 UL Product iQ
File Number: E56070	Yellow Card™	Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets
FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		ANSI/UL 94
1.5 mm, Color: ALL	HB
3.0 mm, Color: ALL	HB
ISO/IEC FLAMMABILITY PROPERTIES	VALUE	TEST METHOD
Flammability		IEC 60695-11-10
1.5 mm, Color: ALL	HB75
3.0 mm, Color: ALL	HB40
ELECTRICAL PROPERTIES	VALUE	TEST METHOD
Hot-wire Ignition (HWI)		UL 746A
1.5 mm	PLC 4
3.0 mm	PLC 4
High Amp Arc Ignition (HAI)		UL 746A
1.5 mm	PLC 0
3.0 mm	PLC 0
Comparative Tracking Index (CTI)	PLC 1	UL 746A
High Voltage Arc Tracking Rate (HVTR)	PLC 0
High Voltage, Low Current Arc Resistance	PLC 7
THERMAL PROPERTIES	VALUE	TEST METHOD
Relative Thermal Index – Electrical Strength		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C
Relative Thermal Index – Mechanical Impact		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C
Relative Thermal Index – Mechanical Strength		UL 746B
1.5 mm	60 °C
3.0 mm	60 °C
		Report Date: 1983-06-23