WONDERLOY PC-385 is a top-notch PC/ABS blend. It can take a beating without breaking, even when it’s cold outside. This material is easy to work with, flowing smoothly to fill molds and create complex shapes. It also keeps its cool under heat, staying firm when things get hot. Manufacturers love it because it’s easy to use and helps them make things faster.
- Application: Automotive interior parts, consumer electronics products, high-end helmets, mobile phone casings, general molding products
- Character: High heat grade, high impact grade, 1.5mm HB
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides. All documents are sourced directly from manufacturers and updated regularly for accuracy.
WONDERLOY® PC-385 Datasheet
| General WONDERLOY® PC-385 | ||||
| Product Description: Ultra high impact | ||||
| Properties | ISO Test Method | Test Condition | Unit | PC-385 |
| Melt Flow Index | 1133 | 260℃×5KG | ml/10 min | 21 |
| Spiral flow | CHIMEI | 260℃,2mm, | cm | 30 |
| V:50%,P:50% | ||||
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.15 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 55 |
| 50 mm/min, break | MPa | 57 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 110 |
| Flexural Strength | 178 | 2 mm/min | MPa | 85 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 2.3 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 55 |
| -30℃, Notched | KJ/m2 | 45 | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 55 |
| -30℃, Notched | KJ/m2 | 45 | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 143 |
| 50℃/hr;5KG | ℃ | 135 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 108 |
| 1.8MPa, annealed | ℃ | – | ||
| Dielectric Constant | IEC 60250 | 1MHz | — | 3 |
| Volume Resistivity | IEC 60093 | — | Ohm X m | 1E+16 |
| Surface Resistivity | IEC 60093 | — | Ohm | 1E+16 |
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 7.5*10⁻⁵ |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.4~0.6 |
| Symbol | 1043 | – | – | >PC+ABS< |
| January 12, 2024 | ||||
WONDERLOY® PC-385 UL Product iQ
| WONDERLOY® PC-385 UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) “WONDERLOY”, furnished as pellets |
| (+) – Indicate 0~0.5% acid scavengers. | ||
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 3 | |
| 3.0 mm | PLC 3 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 0 | |
| 3.0 mm | PLC 0 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746A |
| Dielectric Strength | 32 kV/mm | ASTM D149 |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | |
| Volume Resistivity | 1.0E+14 ohms·cm | ASTM D257/IEC 60093 |
| High Voltage, Low Current Arc Resistance | PLC 7 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| PHYSICAL PROPERTIES | VALUE | TEST METHOD |
| Dimensional Change | 0.0 % | ASTM D1042/ISO 2796 |
| Report Date: 2001-01-12 | ||