WONDERLOY® PC-510 High-flow PC/ABS Resin Material
WONDERLOY PC-510 is a top-notch PC/ABS blend that’s easy to work with. It flows well, making it simple to mold into different shapes. This resin is tough and can take a beating, even in cold weather. It also stands up to heat, which is great for car parts and electronics. Best of all, it’s fire-safe, meeting strict standards.
- Application: Set-top boxes, projectors, computers, communication equipment, consumer electronics products, video game consoles, networking products
- Character: High flow grade, Non-brominated and non-chlorinated flame retardant, 1.5mm V-0, 3.0mm 5VA. (TPP series)
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides. All documents are sourced directly from manufacturers.
WONDERLOY® PC-510 Datasheet
| Flame Retardant WONDERLOY® PC-510 | ||||
| Product Description: High flow | ||||
| Properties | ISO Test Method | Test Condition | Unit | PC-510 |
| Melt Flow Index | 1133 | 260℃×2.16KG | ml/10 min | 21 |
| Spiral flow | CHIMEI | 260℃,2mm, | cm | 45 |
| V:50%,P:50% | ||||
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.17 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 55 |
| 50 mm/min, break | MPa | 45 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 70 |
| Flexural Strength | 178 | 2 mm/min | MPa | 80 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 2.5 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 45 |
| -30℃, Notched | KJ/m2 | – | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 45 |
| -30℃, Notched | KJ/m2 | – | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 94 |
| 50℃/hr;5KG | ℃ | 85 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 73 |
| 1.8MPa, annealed | ℃ | – | ||
| Dielectric Constant | IEC 60250 | 1MHz | — | 3.1 |
| Volume Resistivity | IEC 60093 | — | Ohm X m | 3.9E+15 |
| Surface Resistivity | IEC 60093 | — | Ohm | 2.9E+15 |
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 8*10⁻⁵ |
| Flammability | – | UL-94 | – | 1.5mm V-0 |
| 2.1mm 5VB | ||||
| 3.0mm 5VA | ||||
| Mold Shrinkage | 294-4 | – | % | 0.4~0.6 |
| Symbol | 1043 | – | – | >PC+ABS- |
| FR(40)< | ||||
| January 12, 2024 | ||||
WONDERLOY® PC-510 UL Product iQ
| WONDERLOY® PC-510(a) UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) “WONDERLOY”, furnished as pellets |
| (a) – Ball pressure temperature is in accordance with IEC 60695-10-2 Method B. | ||
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.0 mm, Color: ALL | HB | |
| 1.5 mm, Color: ALL | V-0 | |
| 2.1 mm, Color: ALL | 5VB | |
| V-0 | ||
| 2.5 mm, Color: ALL | 5VB | |
| V-0 | ||
| 3.0 mm, Color: ALL | 5VA | |
| V-0 | ||
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.0 mm, Color: ALL | HB75 | |
| 1.5 mm, Color: ALL | V-0 | |
| 2.1 mm, Color: ALL | V-0 | |
| 2.5 mm, Color: ALL | V-0 | |
| 3.0 mm, Color: ALL | V-0 | |
| Flammability | IEC 60695-11-20 | |
| 2.1 mm, Color: ALL | 5VB | |
| 2.5 mm, Color: ALL | 5VB | |
| 3.0 mm, Color: ALL | 5VA | |
| Glow Wire Ignition Temperature (GWIT) | IEC 60695-2-13 | |
| 1.5 mm | 750 °C | |
| 3.0 mm | 750 °C | |
| Glow Wire Flammability Index (GWFI) | IEC 60695-2-12 | |
| 1.5 mm | 875 °C | |
| 3.0 mm | 960 °C | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 4 | |
| 2.1 mm | PLC 4 | |
| 2.5 mm | PLC 4 | |
| 3.0 mm | PLC 3 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 0 | |
| 2.1 mm | PLC 0 | |
| 2.5 mm | PLC 0 | |
| 3.0 mm | PLC 0 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746A |
| Dielectric Strength | 31 kV/mm | ASTM D149 |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | |
| Volume Resistivity | 1.0E+14 ohms·cm | ASTM D257/IEC 60093 |
| High Voltage, Low Current Arc Resistance | PLC 6 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.0 mm | 60 °C | |
| 1.5 mm | 60 °C | |
| 2.1 mm | 60 °C | |
| 2.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.0 mm | 60 °C | |
| 1.5 mm | 60 °C | |
| 2.1 mm | 60 °C | |
| 2.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.0 mm | 60 °C | |
| 1.5 mm | 60 °C | |
| 2.1 mm | 60 °C | |
| 2.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Ball Pressure Temperature | 75 °C | |
| PHYSICAL PROPERTIES | VALUE | TEST METHOD |
| Dimensional Change | 0.0 % | ASTM D1042/ISO 2796 |
| Report Date: 2001-01-12 | ||