Polylac® PA-765 Flame Retardant High Flow ABS Resin
Chimei Polylac PA-765 ABS Resin is a high-flow, flame-retardant material perfect for thin, precise parts. It meets strict safety standards, ideal for electronics, power panels, car batteries, and appliances. Easy to mold (58 ml/10min melt flow), it saves time and reduces waste. With 38 MPa tensile strength and heat resistance up to 91°C, PA-765 stays tough in hot or cold environments. Trusted for printers, coffee machines, and TV frames, it combines safety, speed, and durability.
- Manufacturer: CHIMEI
- Character: High-flowability, 1.0mm V-1, 1.5mm V-0, 1.5mm 5VB, 2.5mm 5VA (TBBA series)
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.
Polylac® PA-765 Datasheet
| Flame Retardant ABS POLYLAC® PA-765 | ||||
| Product Description: F.R. High flow | ||||
| Properties | ISO Test Method | Test Condition | Unit | PA-765 |
| Melt Flow Index | 1133 | 220℃×10KG | ml/10 min | 58 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.19 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 38 |
| 50 mm/min, break | MPa | 29 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 10 |
| Flexural Strength | 178 | 2 mm/min | MPa | 55 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 1.8 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 21 |
| -30℃, Notched | KJ/m2 | 9 | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 22 |
| -30℃, Notched | KJ/m2 | 10 | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 91 |
| 50℃/hr;5KG | ℃ | 78 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 74 |
| 1.8MPa, annealed | ℃ | 83 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 8.39 x 10-5 |
| Flammability | – | UL-94 | – | 1.0mm V-1 |
| 1.5mm V-0 | ||||
| 1.5mm 5VB | ||||
| 2.5mm 5VA | ||||
| Mold Shrinkage | 294-4 | – | % | 0.3~0.6 |
| Symbol | 1043 | – | – | >ABS-FR(17)< |
| March 11, 2024 | ||||
Polylac® PA-765 UL Product iQ
| POLYLAC® PA-765(+) UL Product iQ | ||
| File Number: E56070 | Yellow Cardâ„¢î ‰ | Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets |
| (+) – Indicate 0~0.5% acid scavengers. | ||
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.0 mm, Color: ALL | V-1 | |
| 1.5 mm, Color: ALL | 5VB | |
| V-0 | ||
| 2.5 mm, Color: ALL | 5VA | |
| V-0 | ||
| 3.0 mm, Color: ALL | 5VA | |
| V-0 | ||
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.0 mm, Color: ALL | V-1 | |
| 1.5 mm, Color: ALL | V-0 | |
| 2.5 mm, Color: ALL | V-0 | |
| 3.0 mm, Color: ALL | V-0 | |
| Flammability | IEC 60695-11-20 | |
| 1.5 mm, Color: ALL | 5VB | |
| 2.5 mm, Color: ALL | 5VA | |
| 3.0 mm, Color: ALL | 5VA | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.0 mm | PLC 4 | |
| 1.5 mm | PLC 2 | |
| 2.5 mm | PLC 2 | |
| 3.0 mm | PLC 0 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.0 mm | PLC 0 | |
| 1.5 mm | PLC 0 | |
| 2.5 mm | PLC 0 | |
| 3.0 mm | PLC 0 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746A |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | |
| Volume Resistivity | 1.0E+15 ohms·cm | ASTM D257/IEC 60093 |
| High Voltage, Low Current Arc Resistance | PLC 7 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.0 mm | 60 °C | |
| 1.5 mm | 80 °C | |
| 2.5 mm | 80 °C | |
| 3.0 mm | 80 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.0 mm | 60 °C | |
| 1.5 mm | 80 °C | |
| 2.5 mm | 80 °C | |
| 3.0 mm | 80 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.0 mm | 60 °C | |
| 1.5 mm | 80 °C | |
| 2.5 mm | 80 °C | |
| 3.0 mm | 80 °C | |