CYCOLOY™ FR Resins C2800

By /
Sabic CYCOLOY™ FR Resins

Sabic Cycoloy FR C2800 (PC/ABS) Resin

Cycoloy Fr resins C2800 (PC/ABS) resin is a non-chlorinated, non-brominated flame retardant material with a UL V0 & 5VB rating. It’s ideal for injection-molded business equipment, monitors, and enclosures requiring safety and performance.

  • Character: non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating
  • Application: business equipment, monitors, and enclosures
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data

  • Tensile Strength (Yield): 58 MPa
  • Flexural Modulus: 2680 MPa
  • Izod Impact (Notched): 427 J/m
  • Heat Deflection Temp (HDT @ 1.82 MPa): 80 °C
  • Vicat Softening Temperature: 90 °C
  • Flammability Rating: UL 94 V-0 (1.47 mm), 5VB
  • Specific Gravity: 1.17
  • Melt Flow Rate: 16 g/10 min
  • Volume Resistivity: 1.E+17 Ω·cm
  • Injection Molding Melt Temperature: 230 – 275 °C
  • Injection Molding Mold Temperature: 50 – 70 °C
  • Injection Molding Drying: 3-4 hours at 75-80 °C

Download

CYCOLOY™ FR Resins C2800 TDS AmericasDownload

Application

  • Business Equipment: Printers, copiers, and scanners.
  • Monitors: Computer and industrial display housings.
  • Enclosures: Electrical cabinets, control boxes, and device covers.

Features & Benefits

Superior Flame Retardancy Without Halogens

This non-chlorinated, non-brominated formula achieves top UL V-0 & 5VB ratings, helping you meet strict safety standards for electronics and business equipment without environmental concerns.

Exceptional Impact Strength and Durability

With high notched Izod impact resistance, Cycoloy FR Resins C2800 creates robust enclosures and monitor housings that can withstand accidental drops and daily physical stress, reducing field failures.

Excellent Thermal and Dimensional Stability

The material maintains its properties and shape across a range of temperatures, ensuring reliable performance for components near heat sources and consistent part dimensions during high-volume molding.

Sabic Cycoloy FR Resins particles

CYCOLOY™ FR C2800 Datasheet

PROPERTIESTYPICAL VALUESUNITSTEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min58     MPaASTM D638
Tensile Strain, yld, Type I, 50 mm/min5     %ASTM D638
Tensile Strain, brk, Type I, 50 mm/min50     %ASTM D638
Tensile Modulus, 50 mm/min2680     MPaASTM D638
Flexural Stress, yld, 2.6 mm/min, 100 mm span96     MPaASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span2680     MPaASTM D790
Hardness, Rockwell R120 –ASTM D785
IMPACT
Izod Impact, notched, 23°C427     J/mASTM D256
Instrumented Dart Impact Total Energy, 23°C58     JASTM D3763
THERMAL
Vicat Softening Temp, Rate B/5090     °CASTM D1525
HDT, 1.82 MPa, 3.2mm, unannealed73     °CASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed80     °CASTM D648
CTE, -40°C to 60°C, flow7.2E-05    1/°CASTM E831
CTE, -40°C to 60°C, xflow7.2E-05    1/°CASTM E831
Thermal Conductivity0.2     W/m-°CASTM C177
Relative Temp Index, Elec80     °CUL 746B
Relative Temp Index, Mech w/impact70     °CUL 746B
Relative Temp Index, Mech w/o impact80     °CUL 746B
PHYSICAL
Specific Gravity1.17 –ASTM D792
Specific Gravity, color1.18 –ASTM D792
Water Absorption, (23°C/24hrs)0.1     %ASTM D570
Water Absorption, (23°C/Saturated)0.4     %ASTM D570
Mold Shrinkage, flow, 3.2 mm0.4 – 0.6    %SABIC method
Mold Shrinkage, xflow, 3.2 mm0.4 – 0.6    %SABIC method
Melt Flow Rate, 260°C/2.16 kgf16     g/10 minASTM D1238
ELECTRICAL
Volume Resistivity1.E+17    Ω .cmASTM D257
Surface Resistivity>1.E+14    ΩASTM D257
Dielectric Strength, in oil, 3.2 mm17.9     kV/mmASTM D149
Relative Permittivity, 50/60 Hz3 –ASTM D150
Relative Permittivity, 100 Hz      3 –ASTM D150
Dissipation Factor, 50/60 Hz      0.0048 –ASTM D150
Arc Resistance, Tungsten {PLC}      6 PLC CodeASTM D495
Hot Wire Ignition {PLC)      3 PLC CodeUL 746A
High Voltage Arc Track Rate {PLC}      3 PLC CodeUL 746A
High Ampere Arc Ign, surface {PLC}      0 PLC CodeUL 746A
Comparative Tracking Index (UL) {PLC}      1 PLC CodeUL 746A
FLAME CHARACTERISTICS
UL Yellow Card LinkE121562-221031––
UL Recognized, 94V-2 Flame Class Rating      0.88 mmUL 94
UL Recognized, 94V-0 Flame Class Rating      1.47 mmUL 94
UL Recognized, 94-5VB Flame Class Rating      2.31 mmUL 94
Oxygen Index (LOI)      35 %ASTM D2863
INJECTION MOLDING
Drying Temperature      75 – 80°C
Drying Time      3 – 4Hrs
Drying Time (Cumulative)      8 Hrs
Maximum Moisture Content      0.04 %
Melt Temperature      230 – 275°C
Nozzle Temperature      230 – 275°C
Front – Zone 3 Temperature      225 – 275°C
Middle – Zone 2 Temperature      215 – 260°C
Rear – Zone 1 Temperature      210 – 255°C
Mold Temperature      50 – 70°C
Back Pressure      0.3 – 0.7MPa
Screw Speed      40 – 70rpm
Shot to Cylinder Size      30 – 80%
Vent Depth      0.038 – 0.076mm

Related CYCOLOY™ fR PC/ABS Products

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top