Valox FR PBT DR48 Flame Retardant Grade

VALOX™ FR resin DR48 is a flame-retardant PBT compound, 17% glass-filled for superior strength. It offers excellent chemical resistance and achieves top UL94 ratings (V-0 at 0.90mm & 5VA at 3.0mm). Perfect for demanding electrical components.

  • Character: 17% glass filled, flame retardant
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data

  • Tensile Strength (Break): 93 MPa
  • Flexural Modulus: 5200 MPa
  • Notched Izod Impact: 49 J/m
  • HDT @1.82 MPa: 182 °C
  • Relative Temp Index (Electrical): 120 °C
  • Volume Resistivity: 1.0E+15 Ω·cm
  • Dielectric Strength (in air): 18.8 kV/mm
  • Comparative Tracking Index (CTI): PLC 3
  • Specific Gravity: 1.53
  • Mold Shrinkage (Flow): 0.4 – 0.6%
  • Melt Temperature: 250 – 265 °C
  • Drying Time: 3 – 4 hours @ 120 °C

Download

VALOX™ FR DR48 Asia TDSDownload

Application

  • Electrical Connectors
  • Bobbins and Coil Formers
  • Switches and Circuit Breakers

Features & Benefits

Superior Flame Retardancy & Safety

This grade delivers reliable UL94 V-0 and 5VA ratings, ensuring critical fire safety in compact, miniaturized electronic designs and protecting both your product and end-users.

Exceptional Strength & Durability

Reinforced with 17% glass fibers, VALOX DR48 provides high rigidity and impact resistance, resulting in robust components that withstand physical stress and last longer.

Reliable Electrical Insulation

With high volume resistivity and dielectric strength, it acts as an effective insulator, preventing electrical failures in connectors and switches for consistent performance.

glass filled VALOX FR PBT resin natural color

Related Valox™ FR PBT Products

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top