Kibilac® PW-997S Extrusion Grade Good Compatibility with PVC
Kibilac® PW-997S ASA is a versatile extrusion-grade resin. It works well for making sheets, car parts, and outdoor items. This plastic is tough and can handle sun and water. It’s easy to work with and mixes nicely with PVC. PW-997S is great for jobs that need a sturdy, long-lasting plastic.
- Application: Extrusion sheet/Automotive parts/Building parts and outdoor application
- Character: Extrusion Grade.Especially good compatibility with PVC.
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.
Kibilac® PW-997S Datasheet
| Extrusion ASA KIBILAC® PW-997S | ||||
| Product Description: Extrusion | ||||
| Properties | ISO Test Method | Test Condition | Unit | PW-997S |
| Melt Flow Index | 1133 | 220℃×10KG | ml/10 min | 4 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.07 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 47 |
| 50 mm/min, break | MPa | 34 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 25 |
| Flexural Strength | 178 | 2 mm/min | MPa | 65 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 2.1 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 20 |
| -30℃, Notched | KJ/m2 | 9 | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 20.5 |
| -30℃, Notched | KJ/m2 | 10 | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 105 |
| 50℃/hr;5KG | ℃ | 94 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 78 |
| 1.8MPa, annealed | ℃ | 96 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 9.3×10-5 |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.4~0.7 |
| Symbol | 1043 | – | – | >ASA< |
Kibilac® PW-997S UL Product iQ
| KIBILAC® PW-997S(+)(f1) UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) “WONDERLOY”, furnished as pellets |
| (f1) – Suitable for outdoor use with respect to exposure to Ultraviolet Light, Water Exposure and Immersion in accordance with UL 746C. | ||
| (+) – Indicate 0~0.5% acid scavengers. | ||
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 4 | |
| 3.0 mm | PLC 3 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 0 | |
| 3.0 mm | PLC 0 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746A |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | |
| High Voltage, Low Current Arc Resistance | PLC 6 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 90 °C | |
| 3.0 mm | 90 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 90 °C | |
| 3.0 mm | 90 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 95 °C | |
| 3.0 mm | 95 °C | |
| PHYSICAL PROPERTIES | VALUE | TEST METHOD |
| UV Exposure & Water Immersion | f1 | UL 746C |