LEXAN™ PC Resin HF4010SR

By /
LEXAN™ PC Resin Sabic Tianjin

SABIC Lexan HF4010SR High Flow

LEXAN™ Resin HF4010SR is a high-flow polycarbonate (42 MFR, MVR 40) engineered for superior mold release, high gloss, and excellent processability. Ideal for large parts and thin-wall molding, it delivers consistent performance in demanding industrial applications.

  • Character: excellent flow 42 MFR, MVR 40, high gloss
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.
=

Typical property data

Mechanical Properties

  • Tensile Strength at Yield: 58 MPa
  • Flexural Modulus: 2,300 MPa
  • Flexural Strength: 90 MPa
  • Tensile Modulus: 2,200 MPa
  • Elongation at Break: 110%

Impact Properties

  • Notched Izod Impact (23°C): 65 kJ/m²
  • Unnotched Izod Impact (23°C): No Break

Thermal Properties

  • Heat Deflection Temp @ 1.82 MPa: 125°C
  • Vicat Softening Temperature: 145°C
  • Thermal Conductivity: 0.2 W/m·K
  • Coefficient of Linear Thermal Expansion: 6.5 x 10⁻⁵ /°C

Physical Properties

  • Mold Shrinkage (Flow): 0.5 – 0.7%
  • Specific Gravity: 1.2
  • Mold Shrinkage (Cross-flow): 0.6 – 0.8%
  • Water Absorption (24h): 0.15%

Flame Performance

  • UL 94 Rating: V-2 at 1.5 mm and 3.0 mm
  • Glow Wire Flammability Index (GWFI): 850°C at 1.0 mm
  • Glow Wire Ignition Temperature (GWIT): 750°C at 1.0 mm

Processing Guidelines

  • Melt Temperature: 280–310°C
  • Mold Temperature: 80–110°C
  • Drying Temperature: 120°C
  • Drying Time: 3–4 hours
  • Injection Speed: High

Download

LEXAN™ HF4010SR Asia TDSDownload
LEXAN™ HF4010SR Americas TDSDownload
LEXAN™ HF4010SR Europe TDSDownload

Associated Documents

Regulatory Data SheetDownload
FMVSS302 General Statement SABIC PetchemDownload
Certified Renewable Polycarbonate BrochureDownload
Certified Renewable Polycarbonate LeafletDownload
LEXAN™ Resin EuropeDownload

Features & Benefits

Excellent Flow for Complex Molds

The high flow rate of LEXAN HF4010SR fills large and thin-walled molds completely, reducing injection pressure and enabling faster cycle times for higher output.

High Impact Strength and Durability

This resin maintains exceptional toughness, even at low temperatures, resulting in reliable parts that withstand drops, impacts, and demanding use in automotive or consumer electronics.

High Gloss & Easy Mold Release

It produces parts with an outstanding aesthetic surface finish straight from the mold, minimizing post-processing and reducing potential for damage during ejection.

LEXAN™ PC Resin

Related Lexan™ Polycarbonate

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top