LEXAN™ PC Resin IR1810

By /
LEXAN™ PC Resin Sabic Tianjin

SABIC Lexan IR1810 High Flow

LEXAN™ Resin IR1810 is a high-flow (MFR = 22 at 300℃/1.2kg), heat-stabilized polycarbonate engineered for custom compounding. It has excellent thermal resistance and processability. It does not contain UV stabilizer or mold release.

  • Character:
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.
=

Typical property data

Mechanical Properties

  • Tensile Strength @ Yield: 60 MPa
  • Tensile Modulus: 2,300 MPa
  • Flexural Strength: 93 MPa
  • Flexural Modulus: 2,300 MPa
  • Elongation @ Break: 110%

Impact Properties

  • Notched Izod Impact @ 23°C: 65 kJ/m²
  • Unnotched Izod Impact @ 23°C: No Break

Thermal Properties

  • Heat Deflection Temperature @ 1.82 MPa: 125°C
  • Vicat Softening Temperature: 148°C
  • Glass Transition Temperature (Tg): 150°C

Physical Properties

  • Melt Flow Rate (300°C/1.2kg): 22 g/10 min
  • Density: 1.2 g/cm³

Flame Performance

  • UL94 Flame Rating: V-2 at 1.5 mm

Processing Guidelines

  • Recommended Processing Temperature: 280–310°C
  • Mold Temperature: 80–110°C
  • Drying Conditions: 120°C for 4 hours

Download

LEXAN™ IR1810 Europe TDSDownload

Associated Documents

Regulatory Data SheetDownload
FMVSS302 General Statement SABIC PetchemDownload
Certified Renewable Polycarbonate BrochureDownload
Certified Renewable Polycarbonate LeafletDownload
LEXAN™ Resin EuropeDownload

Features & Benefits

High Flow for Complex Molds

With a melt flow rate of 22, LEXAN IR1810 enables smooth processing in intricate mold designs, reducing cycle times.

Heat-Stabilized for Durability

Engineered for high thermal resistance, this material maintains structural integrity in elevated processing and service temperatures.

Optimized for Custom Compounding

LEXAN Resin IR1810 provides a clean, additive-free base—ideal for compounders seeking precise control over final formulations.

LEXAN™ PC Resin

Related Lexan™ Polycarbonate

Advanced Manufacturing

Extruder machine
High-speed mixer machine
Water ring pelletizer
Automatic bagging machine
Vibrating screening machine
Plastic rein material warehouse storage capacity
Scroll to Top