Suke PC1003R PC Resin

Suke Plastics PC1003R PC Resin Transparent UV Resistant Grade

Suke PC1003R Polycarbonate resin by Suke Plastics combines transparency, UV resistance, and robust thermal stability for automotive, outdoor, and electronics applications. This Suke modified plastic ensures durability in harsh conditions while meeting critical safety and processing standards.

  • Manufacturer: Suke Plastics
  • Character: Transparent UV Resistant Grade
contact us
Please enable JavaScript in your browser to complete this form.
Click or drag files to this area to upload. You can upload up to 10 files.
* We prioritize your privacy and ensure information security.

Key technical data (ISO)

  • Tensile Strength: 63 MPa
  • Heat Resistance: HDT 138°C @ 0.45 MPa
  • Impact Strength: 800 J/m Notched Izod
  • Flame Rating: UL94 V-2
  • Melt Flow Rate: 10 g/10 min
  • Water Absorption: 0.35%
  • Light Transmission: 88–90%

Download

Suke PC1003R ISO Date SheetDownload

Exceptional Impact Resistance

With an Izod notched impact strength of 800 J/m (ASTM D256), PC PC1003R resin withstands harsh drops and shocks, reducing part failures in devices like smartphone housings or ruggedized connectors.

High-Temperature Stability

It retains structural integrity up to 138°C (HDT, 0.45 MPa), making it ideal for components near heat sources, such as circuit breakers or LED light housings, without warping.

UV-Resistant Clarity

It boasts 88-90% light transmission and <0.8% haze (ASTM D1003), ensuring outdoor electrical enclosures or display panels stay crystal clear and fade-free for years.

Suke PC1003R Transparent UV Resistant Plastic Granular

Application

  • Automotive: Headlamp lenses, dashboards, and connectors.
  • Outdoor Solutions: traffic light casings, and solar panel components.
  • Electronics: Durable router casings, power tool housings, and heat-resistant appliance parts.
  • Appliances: Transparent blender jars and microwave components that resist thermal deformation.

Suke PC1003R Datasheet

UV Resistance Grade Suke PC1003R Data Sheet
Product Description: transparency, UV resistance
MECHANICALTest StandardUnitsTypical Value
Tensile Stress, yld, Type I, 50 mm/minASTM D638MPa63
Tensile Strain, yld, Type I, 50 mm/minASTM D638%6
Tensile Strain, brk, Type I, 50 mm/minASTM D638%>70
Tensile Modulus, 50 mm/minASTM D638MPa2350
Flexural Stress, yld, 1.3 mm/min, 50 mm spanASTM D790MPa90
Flexural Modulus, 1.3 mm/min, 50 mm spanASTM D790MPa2300
Hardness, Rockwell RASTM D785–120
Tensile Stress, yield, 50 mm/minISO 527MPa63
Tensile Strain, yield, 50 mm/minISO 527%6
Tensile Strain, break, 50 mm/minISO 527%>70
Tensile Modulus, 1 mm/minISO 527MPa2350
Flexural Stress, yield, 2 mm/minISO 178MPa90
Flexural Modulus, 2 mm/minISO 178MPa2300
Hardness, Rockwell RISO 2039-2–120
IMPACTTest StandardUnitsTypical Value
Izod Impact, unnotched, 23°CASTM D4812J/mNB
Izod Impact, notched, 23°CASTM D256J/m800
Instrumented Dart Impact Energy @ peak, 23°CASTM D3763J65
Izod Impact, unnotched 80*10*3 +23°CISO 180/1UkJ/m²NB
Izod Impact, unnotched 80*10*3 -30°CISO 180/1UkJ/m²NB
Izod Impact, notched 80*10*3 +23°CISO 180/1AkJ/m²70
Izod Impact, notched 80*10*3 -30°CISO 180/1AkJ/m²12
THERMALTest StandardUnitsTypical Value
Vicat Softening Temp, Rate B/50ASTM D1525℃143
HDT, 0.45 MPa, 3.2 mmASTM D648℃138
HDT, 1.82 MPa, 3.2 mmASTM D648℃127
CTE, -40°C to 95°C, flowASTM E8311/℃7.00E-05
Thermal ConductivityASTM C177W/m-℃0.2
Thermal ConductivityISO 8302W/m-℃0.2
CTE, 23°C to 80°C, flowISO 11359-21/℃7.00E-05
Ball Pressure Test, 125°C +/- 2°CIEC 60695-10-2–Passes
Vicat Softening Temp, Rate B/50ISO 306℃143
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mmISO 75/Bf℃138
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm    ISO 75/Af℃127
PHYSICALTest StandardUnitsTypical Value
Specific GravityASTM D792–1.2
Water Absorption, (23°C/Saturated)ASTM D570%0.35
Mold Shrinkage on Tensile Bar, flowSABIC method%0.5 – 0.7
Mold Shrinkage, flow, 3.2 mmSABIC method%0.5 – 0.7
Melt Flow Rate, 300°C/1.2 kgfASTM D1238g/10 min10
DensityISO 1183g/cm³1.2
Water Absorption, (23°C/saturated)ISO 62-1%0.35
Melt Volume Rate, MVR at 300°C/1.2 kgISO 1133cm³/10 min9
OPTICALTest StandardUnitsTypical Value
Light Transmission, 2.54 mmASTM D1003%88 – 90
Haze, 2.54 mmASTM D1003%<0.8
Refractive IndexASTM D542–1.586
Refractive IndexISO 489–1.586
ELECTRICALTest StandardUnitsTypical Value
Volume ResistivityASTM D257Ω · cm>1.E+15
Dielectric Strength, 1.6 mmASTM D149kV/mm27
Relative Permittivity, 60 HzASTM D150–3
Relative Permittivity, 1 MHzASTM D150–3
Dissipation Factor, 60 HzASTM D150–0.001
Dissipation Factor, 1 MHzASTM D150–0.01
Volume ResistivityIEC 60093Ω · cm>1.E+15
Dielectric Strength, 1.6 mmIEC 60243-1kV/mm27
Relative Permittivity, 60 HzIEC 60250–3
Relative Permittivity, 1 MHzIEC 60250–3
Dissipation Factor, 60 HzIEC 60250–0.001
Dissipation Factor, 1 MHzIEC 60250–0.01
FLAME CHARACTERISTICSTest StandardUnitsTypical Value
UL Recognized, 94V-2 Flame Class RatingUL 94mm1.6
INJECTION MOLDINGRANGE
Drying Temperature120 ℃
Drying Time2 – 4 Hrs
Maximum Moisture Content0.0002
Melt Temperature280 – 310 ℃
Nozzle Temperature270 – 290 ℃
Front – Zone 3 Temperature280 – 310 ℃
Middle – Zone 2 Temperature270 – 290 ℃
Rear – Zone 1 Temperature260 – 280 ℃
Hopper Temperature60 – 80 ℃
Mold Temperature  80 – 110 ℃

Related Suke Plastics PC Plastics

Advanced Manufacturing