Polylac® PA-757F Low Residual Monomer Food Use ABS
POLYLAC® PA-757F ABS resin is a food-safe, high-performance plastic perfect for kitchenware, toys, and household items. With low monomer residue (EU 10/2011 certified), it combines safety, strength, and easy processing for reliable, everyday products.
- Character: Low monomer residue (EU 10/2011 Certification)
- Application: Food containers, kettles, kitchenware, toys
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.
Polylac® PA-757F Datasheet
| Low Residual Monomer ABS POLYLAC® PA-757F | ||||
| Product Description: Low residual monomer, Food application | ||||
| Properties | ISO Test Method | Test Condition | Unit | PA-757F |
| Melt Flow Index | 1133 | 220℃×10KG | ml/10 min | 18 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.05 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 47 |
| 50 mm/min, break | MPa | 34 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 40 |
| Flexural Strength | 178 | 2 mm/min | MPa | 76 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 2.2 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 19 |
| -30℃, Notched | KJ/m2 | 9 | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 21 |
| -30℃, Notched | KJ/m2 | 10 | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 104 |
| 50℃/hr;5KG | ℃ | 100 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 83 |
| 1.8MPa, annealed | ℃ | 98 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 8.6 x 10-5 |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.4~0.7 |
| Symbol | 1043 | – | – | >ABS< |
| March 11, 2024 | ||||
Polylac® PA-757F UL Product iQ
| POLYLAC® PA-757F UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets |
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 4 | |
| 3.0 mm | PLC 3 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 0 | |
| 3.0 mm | PLC 0 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746A |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | |
| High Voltage, Low Current Arc Resistance | PLC 7 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 85 °C | |
| 3.0 mm | 85 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 80 °C | |
| 3.0 mm | 80 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 85 °C | |
| 3.0 mm | 85 °C | |