Polylac® PA-703 TRP Transparent Medical Grade MABS Resin
Polylac PA-703 TRP is a medical-grade MABS resin that meets ISO 10993 biocompatibility standards, making it ideal for medical device manufacturing. This specialized material features excellent transparency with a distinctive blue tint, alongside superior chemical resistance that maintains integrity in medical environments.
- Character: Transparency with blue tint, chemical resistance, comply with Bio-compatibility test (ISO10993)
- Application: Medical application
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.
Polylac® PA-703 TRP Datasheet
| Medical MABS POLYLAC® PA-703 TRP | ||||
| Product Description: ISO 10993, Transparent ,Chemical resistant | ||||
| Properties | ISO Test Method | Test Condition | Unit | PA-703 TRP |
| Melt Flow Index | 1133 | 200℃×5KG | ml/10 min | 2.3 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.08 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 47 |
| 50 mm/min, break | MPa | 33 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 50 |
| Flexural Strength | 178 | 2 mm/min | MPa | 62 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 2.1 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 15 |
| -30℃, Notched | KJ/m2 | 8 | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 15 |
| Charpy -30℃, Notched | KJ/m2 | 8 | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 102 |
| 50℃/hr;5KG | ℃ | 94 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 75 |
| 1.8MPa, annealed | ℃ | 95 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 8.7 x 10-5 |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.3 ~ 0.7 |
| Symbol | 1043 | – | – | >MABS< |
| July 22, 2021 | ||||
Polylac® PA-703 TRP UL Product iQ
| POLYLAC® PA-703 TRP UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Methyl Methacrylate Acrylonitrile Butadiene Styrene (MABS) “POLYLAC”, furnished as sheets |
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 3 | |
| 3.0 mm | PLC 3 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 0 | |
| 3.0 mm | PLC 0 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746A |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | |
| High Voltage, Low Current Arc Resistance | PLC 5 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 50 °C | |
| 3.0 mm | 50 °C | |