LEXAN™ PC Resin 241S

By /
LEXAN™ PC Resin Sabic Tianjin

SABIC Lexan 241S Flame Retardant Grade

LEXAN 241S is a high-performance polycarbonate (PC) resin with a 10.5 MFR, offering improved flame retardance and excellent mold release. Ideal for applications requiring dimensional stability, safety, and efficient processing.

  • Character: 10.5 MFR. Improved flame retardance. Super mold release.
contact us
Drag & Drop Files, Choose Files to Upload You can upload up to 10 files.
* We prioritize your privacy and ensure information security.
=

Key technical data

  • Melt Flow Rate (300°C/1.2 kg): 10.5 g/10 min
  • Tensile Strength at Break: 68 MPa
  • Notched Izod Impact (23°C): 801 J/m
  • Flexural Modulus: 2340 MPa
  • Specific Gravity: 1.20
  • Water Absorption (24 hrs): 0.15%
  • Heat Deflection Temp (1.82 MPa): 132°C
  • Vicat Softening Temperature: 154°C
  • Relative Temperature Index (Electrical & Mechanical): 130°C
  • Light Transmission (2.54 mm): 88%
  • Haze (2.54 mm): 1%
  • Volume Resistivity: >1.5E+17 Ω·cm
  • Dielectric Strength: 14.9 kV/mm
  • UL 94 Rating: V-0 (@ 5.99mm thickness), V-2 (@ 1.09mm thickness)
  • Melt Temperature: 295 – 315 °C
  • Mold Temperature: 70 – 95 °C
  • Drying: 120°C for 3-4 hours (Moisture <0.02%)

Download

LEXAN™ 241S Asia TDSDownload

Features & Benefits

Enhanced Flame Resistance

Flame-retardant formulation meets UL94 V-0 at 1.5mm—ideal for electrical housings and devices requiring strict fire safety compliance.

Superior Mold Release

Excellent mold release properties reduce cycle times and tool wear—perfect for high-volume injection molding operations.

High Flow for Complex Molds

10.5 MFR supports intricate part designs and thin-wall molding—enabling engineers to push design boundaries without sacrificing performance.

LEXAN™ PC Resin

Related Lexan™ Polycarbonate Products

Advanced Manufacturing