Suke FR965 ABS Resin Flame Retardant Grade

Suke FR965 ABS Resin Flame Retardant Grade

Suke FR965 ABS resin delivers exceptional fire safety with V0 flame retardancy (1.5mm) thanks to TBBPA. Offering high flow (MFR 50 g/10min) and balanced mechanical strength, it’s the reliable choice for printers, electronics, and office equipment components.

Manufacturer: Suke Plastics
Character: A/TBBPA, High flame retardant
Application: printer; Electrical &electronic; Office supplies

ABS Resin

Key technical data (ASTM)

Flame Retardancy: UL94 V-0 @ 1.5mm
Melt Flow Rate (MFR): 50 g/10 min (220°C / 10.0 kg)
Density: 1.19 g/cm³
Tensile Strength: 40 MPa
Flexural Strength: 68 MPa
Flexural Modulus: 2100 MPa
Impact Strength (Izod Notched): 18 kJ/m² (3.2mm, 23°C)
Heat Deflection Temp (HDT): 77 °C (@ 0.45 MPa, 6.4mm)
Processing Drying: 80°C for 3 hours recommended
Processing Melt Temperature: ~200°C
Processing Max Processing Temp: 220°C
Processing Mold Temperature: ~70°C

Download

Suke FR965 ABS plastic application Download

Application

Printer Components: Housings, internal frames, paper trays, covers.
Electrical & Electronic Parts: Connectors, sockets, enclosures, internal supports, terminal blocks.
Office Supplies: Copier housings, computer accessory casings, equipment covers, robust organizers.

Features & Benefits

Top-Tier Fire Safety

It achieves UL94 V-0 rating at just 1.5mm thickness, providing critical protection against fire hazards in sensitive electronic and office environments. Essential for safety compliance.

Excellent Flow & Processability

High Melt Flow Rate (50 g/10min @220°C/10kg) ensures easy filling of complex, thin-walled molds, boosting production efficiency and part quality for intricate designs.

Balanced Strength & Stiffness

It combines good tensile strength (40 MPa) and high flexural modulus (2100 MPa) for durable parts that resist deformation under load, ideal for structural components.

Suke Plastics FR965 ABS Resin