Polylac® PA-758 Transparent High Flow MABS Resin
Polylac PA-758 is a transparent versatile MABS plastic resin with excellent qualities. It’s easy to mold and has good clarity. This material is tough and can handle impacts well. It’s great for making things like air conditioner panels, 3C product casings, and even stationery. The material stays strong in different temperatures. It’s also fire-resistant, meeting UL-94 HB standards at 1.5mm thickness.
- Application: Air conditioning panels, washing machine covers, vacuum cleaner casings, 3C product casings, household appliances, stationery
- Character: Good transparency, high flowability
Download
Access essential product documentation including technical data sheets, safety information, environmental certifications, and processing guides.
All documents are sourced directly from manufacturers and updated regularly for accuracy.
Polylac® PA-758 Datasheet
| Transparent MABS POLYLAC® PA-758 | ||||
| Product Description: Transparent | ||||
| Properties | ISO Test Method | Test Condition | Unit | PA-758 |
| Melt Flow Index | 1133 | 200℃×5KG | ml/10 min | 3 |
| Mass Density | 1183 | 23 ℃ | g/cm3 | 1.08 |
| Tensile Strength | 527 | 50 mm/min, yield | MPa | 42 |
| 50 mm/min, break | MPa | 33 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 35 |
| Flexural Strength | 178 | 2 mm/min | MPa | 57 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 1.9 |
| Izod Impact Strength | 180/1A | 23℃, Notched | KJ/m2 | 14 |
| -30℃, Notched | KJ/m2 | 7 | ||
| Charpy Impact Strength | 179 | 23℃, Notched | KJ/m2 | 14 |
| -30℃, Notched | KJ/m2 | 7 | ||
| Vicat Softening Temp. | 306 | 50℃/hr;1KG | ℃ | 104 |
| 50℃/hr;5KG | ℃ | 96 | ||
| Heat Distortion Temp. | 75/A | 1.8MPa, unannealed | ℃ | 77 |
| 1.8MPa, annealed | ℃ | 97 | ||
| Coefficient of Linear Thermal Expansion | 11359 | – | – | 9.0 x 10-5 |
| Flammability | – | UL-94 | – | 1.5mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.3 ~ 0.7 |
| Symbol | 1043 | – | – | >MABS< |
Polylac® PA-758 UL Product iQ
| POLYLAC® PA-758 UL Product iQ | ||
| File Number: E56070 | Yellow Card™ | Acrylonitrile Butadiene Styrene (ABS) “POLYLAC”, furnished as pellets |
| FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | ANSI/UL 94 | |
| 1.5 mm, Color: ALL | HB | |
| 3.0 mm, Color: ALL | HB | |
| ISO/IEC FLAMMABILITY PROPERTIES | VALUE | TEST METHOD |
| Flammability | IEC 60695-11-10 | |
| 1.5 mm, Color: ALL | HB75 | |
| 3.0 mm, Color: ALL | HB40 | |
| ELECTRICAL PROPERTIES | VALUE | TEST METHOD |
| Hot-wire Ignition (HWI) | UL 746A | |
| 1.5 mm | PLC 4 | |
| 3.0 mm | PLC 3 | |
| High Amp Arc Ignition (HAI) | UL 746A | |
| 1.5 mm | PLC 3 | |
| 3.0 mm | PLC 3 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746A |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | |
| High Voltage, Low Current Arc Resistance | PLC 6 | |
| THERMAL PROPERTIES | VALUE | TEST METHOD |
| Relative Thermal Index – Electrical Strength | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Relative Thermal Index – Mechanical Impact | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |
| Relative Thermal Index – Mechanical Strength | UL 746B | |
| 1.5 mm | 60 °C | |
| 3.0 mm | 60 °C | |